Corrosion Behaviors of Q235 Steel in Seawater Containing Sulfate-Reducing Bacteria

Zhi-quan Yang,Shao-qi Zhou,Guang-zhou Liu,Cun-guo Lin

DOI: https://doi.org/10.3321/j.issn:1000-565X.2009.10.026

2009-01-01

Abstract:In order to better reveal the mechanism of microbiological corrosion, the corrosion behaviors of mild steel Q235 in marine conditions with/without sulfate-reducing bacteria (SRB) were investigated via such electrochemical methods as the corrosion potential, the polarization curve, the electrochemical impedance spectrometry and the environmental scanning electron microscopy. The results show that (1) due to the existence of SRB, the corrosion potential of Q235 steel in marine conditions rapidly shifts to the passive potential region until it is gradually stabilized at a value of about -740 mV; (2) in the marine condition with SRB, both the corrosion current density and the corrosion rate increase, while the polarization resistance becomes lower; and (3) after the microbiological corrosion, there forms a large amount of holes on the surface of Q235 steel, which shows the occurrence of heavy pitting corrosion.