Abstract:Rare earth/transition metal multilayers with tunable net magnetization (Mnet) and perpendicular magnetic anisotropy (PMA) are potential systems for achieving devices with high speed and density. In this paper, we perform a detailed study on the temperature (T) and thickness dependences of perpendicular magnetic properties in [Co80Fe20 (0.45 nm)/Tb (x = 0.3-0.95 nm)]5 multilayers. The strong antiferromagnetic (AF) interaction between Tb and CoFe spins is demonstrated at the interfaces, and the magnetization compensation thickness (at which Mnet tends to zero) is determined as x similar to 0.6 nm at room temperature. Whether the multilayer is Tbrich or CoFe-rich, an increasing trend in magnetic coercivity is found with the decrease in T, demonstrating that the Mnet of the AF-coupled region is always dominated by CoFe in this structure. Furthermore, the transient polar MOKE signals were also measured at elevated T by using laser pulse heating. With the increase in pump fluence, the original rectangle loop changes to a two-step switching shape for the sample with 0.4 nm Tb due to the decreased PMA strength and increased interfacial atomic diffusion. However, for the multilayer with 0.9 nm Tb that is farther from compensation, the loop becomes very inclined since the PMA is relatively weak and nearly vanishes upon laser impulsion. These results provide a deep insight into the key roles of sublayer thicknesses and interfaces, which are very helpful for achieving efficient control of the spintronic devices based on the AF-coupled materials.

The Influence of Underlayers on the Magnetic Properties of TbFeCo Films for Hybrid Recording

Effect of Ta Underlayer on Perpendicular Anisotropy of TbFeCo Films

Coercivity, Microstructure and Magnetization Reversal Mechanism in Tini-Doped L1(0) Fept Thin Films

Influence of Intermediate Layer on Magnetic Properties of $l1_{0}$ordered FePt Perpendicular Recording Media

Influence of FeCo-rich Crystallites on the Magnetic Properties of Amorphous TbFeCo Thin Films

Fabrication of TbFeCo alloy films with tunable perpendicular coercivity evaluated by extraordinary Hall effect measurements

Low-temperature Deposition of L10 FePt Films for Ultra-High Density Magnetic Recording

Development of ${\rm L}1_{0}$ FePt:C (001) Thin Films with High Coercivity and Small Grain Size for Ultra-High-Density Magnetic Recording Media

Interlayer antiferromagnetic coupling in Tb3Fe5O12/Y3Fe5O12 bilayers

Magnetic Properties of Fe/Pt Films by Symmetrical Insertion of Ag

Investigation of Microstructure and Soft Magnetic Properties of Fe65Co35 Thin Films Deposited on Different Underlayers

The magnetic and magneto-optical properties of PtFe–Co multiulayers

Antiferromagnetic Coupling and Perpendicular Anisotropy in TbFeCo∕NiO Multilayers

Temperature Dependence of Magnetic Properties in CoFe/Tb Multilayers with Perpendicular Magnetic Anisotropy

Interlayer Antiferromagnetic Coupling in Tb3Fe5O12/Y3Fe5O< Sub>12 Bilayers

Magnetic Phases and Exchange Coupling in TbFeCo Films

CoPt/Ag(Cu) Nanocomposite Films for Ultra-High Density Perpendicular Magnetic Recording Media

Influence of film structure on the perpendicular magnetic anisotropy in Fe/Tb multilayers

Granular L10 FePt:TiO2 (001) nanocomposite thin films with 5nm grains for high density magnetic recording

Influence of Film Roughness on the Soft Magnetic Properties of Fe/Ni Multilayers

Investigation and Effective Control of Perpendicular Magnetic Anisotropy for Tbco Films with Different Underlayers