Abstract:The core-shell CdTe/ZnS quantum dots were prepared with an improved process in aqueous phase. CdTe QDs were synthesized under conditions of pH 9.1, 96 °C, refluxing for 5h, and which was used as core material; ZnS was formed as shell material to enhance the optical properties. Optical properties were characterized with fluorescence spectrum (FS), and morphology of QDs was investigated via transmission electron microscopy (TEM) method. Moreover, composition and formation of CdTe/ZnS core-shell QDs was characterized via x-ray diffraction (XRD) method. Optimum conditions were investigated to obtain the qualified CdTe/ZnS core-shell QDs, the results indicated QDs with high quantum yields and fluorescence intensity were achieved under conditions of pH 9.0, 45 °C, refluxing for 1h, and v/v/v ratio of CdTe/Na2S/ZnSO4 is 4/1/1. The TEM data indicated that average size of 5 nm CdTe core was prepared, and CdTe/ZnS core-shell QDs with average size of 11 nm were achieved under the optimum conditions. ca 30nm of red shift of a maximum emission wavelength from ca 530 nm (CdTe) to 560 nm (CdTe/ZnS) was observed via FS under the optimum conditions, which inferred the growth of QDs and formation of ZnS shells. Furthermore, the enhanced fluorescence intensity of CdTe/ZnS core-shell QDs was detected and over two times of fluorescence intensity was increased after formation of ZnS shell. The obtained QDs will have great potential application in biological researches and biosensing system based on fluorescence resonance energy transition (FRET).

Luminescent nanoparticles of silica-encapsulated cadmium-tellurium (CdTe) quantum dots with a core-shell structure: Preparation and characterization

Preparation and characterization of CdTe@SiO2 core/shell luminescent composite nanoparticles

Silica Coating Of Water-Soluble Cdte/Cds Core-Shell Nanocrystals By Microemulsion Method

Synthesis and Characterization of CdTe@CdS Quantum Dots Layered on Silica Nanoparticles

Preparation of CdSe/CdS/SiO2 nanospheres and their luminescent properties

Silica Coating of Luminescent Quantum Dots Prepared in Aqueous Media for Cellular Labeling

Preparation of Highly Luminescent CdTe/CdS Core/Shell Quantum Dots

Preparation and Luminescent Properties of CdSe and Core-Shell CdSe/CdS Quantum Dots in Aqueous Solution

Facile Synthesis and Characterization of Highly Fluorescent and Biocompatible N-acetyl-L-cysteine Capped CdTe/CdS/ZnS Core/shell/shell Quantum Dots in Aqueous Phase.

An Enhanced Luminescent Cdte/Zns Core-Shell Quantum Dot: Synthesis, Characterization, and Its Optical Properties

Preparation, Characterization and Application of Water-soluble CdTe Luminescent Probes

Coating aqueous quantum dots with silica via reverse microemulsion method: Toward size-controllable and robust fluorescent nanoparticles

Luminescence Stability of the Silica Encapsulated CdSe Quantum Dots&#

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

Synthesis of Aqueous CdTe Quantum Dots Embedded Silica Nanoparticles and Their Applications As Fluorescence Probes

Preparation Of Strongly Fluorescent Silica Nanoparticles Of Polyelectrolyte-Protected Cadmium Telluride Quantum Dots And Their Application To Cell Toxicity And Imaging

Aqueous Synthesis and Fluorescence-Imaging Application of Cdte/Znse Core/Shell Quantum Dots with High Stability and Low Cytotoxicity

Study on the Luminescence Stability of CdSe/CdxZn1-xS Quantum Dots During the Silication Process

Facile Synthesis of Near-Infrared-emitting Water-Dispersed CdHgTe/CdS/ZnS Core/Shell/Shell Quantum Dots

The Preparation of Cdte Nanoparticles and Cdte Nanoparticle-Label Led Microspheres for Biological Applications

A Facile Way to Fabricate CdSe Quantum Dots Coated with Silica and the Fluorescence Property