Electrical Transport and Thermoelectric Properties of Y1−xCaxCoO3 (⩽x⩽0.1) at High Temperatures
Y. Liu,X. Y. Qin,H. X. Xin,J. Zhang,H. J. Li,Y. F. Wang
DOI: https://doi.org/10.1063/1.2721381
IF: 2.877
2007-01-01
Journal of Applied Physics
Abstract:The effects of Ca substitution for Y on the electrical transport and thermoelectric properties of Y1-xCaxCoO3 (0 <= x <= 0.1), prepared by using the sol-gel process, were investigated in the temperature range from 300 to 780 K. The results indicated that direct current electrical resistivity rho of Y1-xCaxCoO3 decreased remarkably with increasing Ca content x as x <= 0.01, which could mainly be attributed to the increase of hole concentration due to substitution of Ca2+ for Y3+. The temperature dependences of the resistivity for Y1-xCaxCoO3 were all found to be basically consistent with small-polaron hopping conduction model. Although Seebeck coefficient S of Y1-xCaxCoO3 at low temperatures T <similar to 550 K decreased remarkably with increasing x, it approached a limit value similar to 150 mu V/K at similar to 800 K for all the samples with different x, which was consistent well with the thermopower resulting from the degeneracy of electron configuration estimated from Heikes formula by assuming that Co3+ and Co4+ exist in low spin state. Experiments showed that thermal conductivity kappa of Y1-xCaxCoO3 came mainly from its lattice component, whose decrease with increasing x could be chiefly ascribed to impurity-scattering effect due to Ca doping. The thermoelectric figure of merit ZT (=(ST)-T-2/rho kappa) of Y1-xCaxCoO3 changed nonmonotonously with increasing doping content of Ca, and Y0.95Ca0.05CoO3 was found to have optimum thermoelectric properties with ZT=0.019 at 660 K, which was about ten-fold greater than that of YCoO3, indicating that its thermoelectric properties could be improved effectively by appropriate substitution of Ca for Y in this compound. (c) 2007 American Institute of Physics.