Abstract:Small amount of Nickel deposited on SiO 2 support by electroless plating was verified to have a significant promoting effect on the catalytic performance of the K 2 MoO 4 /SiO 2 catalyst for methanethiol synthesis from H 2 S-rich synthesis gas. The addition of Nickel was found to be in favor of the suppression of the CO 2 formation. The results of BET, TPR and Raman characterizations for the Ni-modified SiO 2 and the catalyst K 2 MoO 4 /Ni-SiO 2 showed that the surface properties of Ni-modified SiO 2 were similar to those of unmodified SiO 2 and that no Raman characteristic band specific to NiO from the catalyst K 2 MoO 4 /Ni-SiO 2 was detected. For oxidic K 2 MoO 4 /Ni-SiO 2 catalyst lower reduction temperature was measured. For sulfided catalysts, reduced molybdenum oxides and oxysulfides were detected, which was inferred to be closely related to high catalytic activity of the catalyst.

Study on Methanethiol Synthesis from H 2 S-Rich Syngas Over K 2 MoO 4 Catalyst Supported on Electrolessly Ni-Plated SiO 2