Nonlinear Optical Properties of Poly‐ortho‐toluidine Films Implantated by N+ Ions with Different Energy

Yan Shaolin,Wu Hongcai,Gao Song
DOI: https://doi.org/10.1002/pc.20718
IF: 5.2
2009-01-01
Polymer Composites
Abstract:This article reports experimental work on the effect of N+ ion implantation on third-order nonlinear optical properties of POT films. Using K2Cr2O7 as oxidizing agent, poly-ortho-toluidine (POT) was synthesized in 1 M hydrochloric. The POT films were prepared by spin-coating method and then implantated by N+ ions (15-30 KeV) at a dose 1.9 x 10(16) ions/cm(2). The films were characterized by FT-IR spectroscopy, visible spectroscopy and SEM, their third-order nonlinear optical susceptibility (chi((3))) were also examined by a degenerate four-wave mixing (DFWM) system at 532nm. Compared to pristine POT films, the optical band gap obtained from visible spectra decreased from 3.58 to 3.48 eV when the energy was 30 KeV. Also, The chi((3)) value of implantated POT films increased from 3.31 x 10(-10) esu to 4.04 x 10(-9) esu when the implantated energy was 25 KeV. POLYM. COMPOS., 30:1492-1496, 2009. (C) 2008 Society of Plastics Engineers
What problem does this paper attempt to address?