Synthesis and compositional analysis of poly(lactic acid-co-3-phenylmethyl- 2, 5-morpholinedione)

Ying Liu,RongQing Wei,Xiaoning Liu

2009-01-01

Acta Polymerica Sinica

Abstract:In the first step, 3-phenylmethyl-2, 5-rnorpholinedione (PMD) was synthesized by using phenylalanine as the raw material. In the second step, poly (lactic acid-co-3-phenylmethyl-2, 5-morpholinedione) was prepared by ring-opening copolymerization of PMD and lactide (LA). Stannous octanoate was used as catalyst in the reaction of second step. The structure of copolymers was analyzed by IR, 1H-NMR and DSC. The contents of copolymers were detected by infrared spectroscopy instead of 1H-NMR. Two characteristic peaks at 1671.53 cm -1 and 870.82 cm -1 were selected for PMD and PLA in IR. A standard working curve was established: Y = 0.05567X + 0.1091 (r = 0.9993), where X was the reciprocal of PMD monomer molar concentration, and Y was the absorbance ratio of PLA to PMD at their characteristic peaks. Effects of catalyst content, reaction time and temperature on the concentration of PMD and [η] in copolymers were studied. It was found that, with prolonging of reaction time, the [η] was first increased then decreased under the condition of low catalyst concentration. Furthermore, under the condition of high catalyst concentration, the [η] suspended during 10 h because of the formation of amide linkage products which are more stable. The concentration of PMD in resulting copolymers increases linerly with the increase of PMD in feed. The PMD was less ring-opening reactive than LA, so it was difficult to incorporate the phenyls into the copolymer. However, under the condition of low feed ratio, the contents of PMD can increase when the temperature becomes higher. Moreover, with increasing the concentration of PMD in copolymer, the influence of catalyst content and temperature on copolymer decreased by the stability of phenyl.