Structure and Magnetism of Fe Nanowires Array Prepared by Electrochemical Deposition with AAO Template

JIANG Hai-bo,GU Feng,LI Chun-zhong
DOI: https://doi.org/10.3321/j.issn:1009-606x.2008.02.031
2008-01-01
Abstract:A two-step electrochemical anodizing approach was introduced to prepare porous anodic aluminum oxide(AAO) membrane in sulfuric acid solution.The SEM image shows that the pore diameter is 20 nm,interpore spacing 50 nm and pore density 4.5×1010 pores/cm2.Ordered Fe nanowire arrays embedded in AAO template have been fabricated by pulse voltage electrodeposition of Fe into the pores of AAO.The Rietveld results show that the preferred orientation of those nanowires with diameter of 20 nm is crystal plane of Fe(110) and preferred orientation factor is 0.30.The easy magnetization axis of this system is perpendicular to the membrane.When the outer magnetic field is perpendicular to the membrane,the squareness is as high as 0.914,and coercivity 1656 Oe.