Abstract:The changes in optical properties and damage mechanism of ZnO/silicone white paint caused by <200 keV protons in space were investigated in terms of ground-based simulation testing. The energies of protons were chosen as 50, 90, and 110 keV. The results show that the change in solar absorptance Δαs increases with increasing irradiation fluence as well as the proton energy. On the basis of photoluminescence spectroscopy, it is revealed that with increasing proton fluence, the 660-nm emission band related to the interstitial Zn-ions changes little, the 405-nm emission band related to the Zn vacancies decreases and tends to disappear, the 460-nm emission band related to the double ionized oxygen vacancies V··o decreases, and the emission band related to the singly ionized oxygen vacancies V·o increases. SRIM simulation analysis indicates that the damage effect of ZnO/silicone white paint caused by proton exposure would be aggravated due to the organic silicone binder. The proton irradiation leads to ionization of Zn atoms, formation of free oxygen and oxygen vacancies, and degradation of the organic silicone binder. It is believed that the optical degradation of ZnO/silicone white paint, induced by <200 keV protons, can be attributed to the combined effect of these three processes.

Effects of low energy protons on optical degradation of ZnO white paint

Formation and evolution of oxygen vacancies in ZnO white paint during proton exposure

Slow-positron annihilation analysis on optical degradation of ZnO white paint irradiated by protons

An Analysis on Optical Degradation of ZnO/silicone White Paint under Proton Exposure

A Study on Damage Effects of <200 Kev Protons on ZnO/silicone White Paint

Study on damage effects of low energy protons on ZnO/silicone white paint using infrared spectrum

The optical degradation of ZnO-pigmented white paint induced by the combined electron-plus-proton irradiations

Optical degradation of silicone in ZnO/silicone white paint irradiated by <200keV protons

The damage of ZnO powder caused by proton irradiation

The Degradation Kinetics of the Optical Properties under Proton Irradiation for Zno Pigments Modified by Al2o3 and Al2o3 Center Dot Ceo2 Nanopowders

Proton Irradiation Effects on Zno Pigments Modified by Zro2 Nanopowders

Ground Recovery and Conservation of Property Degradation of ZnO-pigmented White Paints in Space

Study of the Degradation and Recovery of the Optical Properties of H+-implanted ZnO Pigments

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Influence of Proton Irradiation on the Photoluminescence Spectra of Zinc Oxide Modified by ZrO2 and ZrO2·Y2O3 Nanopowders

The Effects of Oxygen Partial Pressure and Substrate Temperature on the Structural and Optical Properties of Zno Films

Comparison of the optical property degradation of oxide micro- and nanopowders irradiated by 100 keV protons

Proton and Electron Irradiation Induced Changes in the Optical Properties of Zno Pigments Modified with Zro2 and Al2o3 Nanopowders

Simulations of the radiation damage in S781 white paint induced by low-energy protons

Degradation of the Optical Properties of Zinc-Oxide Micropowders and Nanopowders under Proton and Electron Irradiation

Degradation of the Optical Properties of Two-Layer Hollow ZnO/SiO 2 Particles after Irradiation with Protons