Low-Threshold and Broadly Tunable Lasers of Yb(3+)-Doped Yttrium Lanthanum Oxide Ceramic

Qiang Hao,Wenxue Li,Heping Zeng,Qiuhong Yang,Chuanguo Dou,Hongxu Zhou,Wei Lu

DOI: https://doi.org/10.1063/1.2926654

IF: 4

2008-01-01

Applied Physics Letters

Abstract:We experimentally demonstrated diode-pumped continuous wave and tunable laser operation of Yb3+-doped yttrium lanthanum oxide transparent ceramic [Yb:(Y1−xLax)2O3,x=0.1], which was fabricated with nanopowders and sintered in H2 atmosphere. As low as 400mW pumping threshold and a slope efficiency of 52% were realized at 1080nm under a high-brightness 976nm diode pump with a fiber core of 50μm and a numerical aperture of 0.22. A maximum output power of 2.1W was obtained when the non-lasing absorbed pump power was 19.5W at 976nm with diode laser of 400μm fiber core. A smooth tunable curve from 1018to1086nm was achieved at 940nm diode pump. Broadband lasing spectra up to 30nm were observed in the tunable laser experiment.