Bi3+/Mn4+ co‐doped dual emission phosphors for potential plant lighting
Sheng Wu,Quan Liu,Mikhail G. Brik,Puxian Xiong,Dong Wang,Guoxing Zhang,Yan Chen
DOI: https://doi.org/10.1111/jace.18551
IF: 4.186
2022-05-20
Journal of the American Ceramic Society
Abstract:Developing environment‐friendly dual‐emission phosphors of both blue‐cyan and deep‐red lights is desirable for the utilized indoor plant lighting research. Notably, the naked 6s and 6p Bi3+ ions are sensitive to the lattice sites, which emits from UV to red lights in various crystal compounds. Meanwhile, the 2E→4A2g transition of Mn4+ ions promises its deep‐red light emissions, which satisfies the demand for specific wavelength lights for plants growth. Hence, a Bi3+/Mn4+ co‐doped Sr2LaGaO5: Bi3+,Mn4+ (SLGO:Bi3+,Mn4+) phosphor was finally synthesized. The phase, micro‐morphology and luminescent properties were systematically evaluated. Upon excitation at 350 nm light, dual emissions of both blue‐cyan (470 nm) and deep‐red (718 nm) lights were observed. Besides, due to the pronounced PL spectral overlap between Bi3+ and Mn4+ ions, a potential energy transfer process from Bi3+ to Mn4+ ions was confirmed. The relative PL intensities between Bi3+ and Mn4+ ions can be tuned just by adjusting the Mn4+ ion concentration. Besides, Li+ codoping has been evidenced to improve the deep‐red emissions (718 nm) of SLGO:0.005Mn4+ due to charge compensation and rationally designed lattice distortion, together with the improved thermal stability. Finally, the emissions of SLGO:Bi3+,Mn4+,Li+ phosphor suit properly with the absorption of the four fundamental pigments for plant growth, indicating that the prepared phosphorescent materials may have a prospect in plant light‐emitting diodes (LEDs) lighting. This article is protected by copyright. All rights reserved
materials science, ceramics