Studies on the preparation and properties of LiNbO2 modified KNN lead-free piezoelectric ceramics

Lang Wu,Dingquan Xiao,DunMin Lin,Jianguo Zhu,Ping Yu,Xiang Li,Yong Sun,Yan Zhuang,Qun Wei

2008-01-01

Abstract:LiNbO3 modified K0.5Na0.5NbO3 (abbreviated as KNN + xLN, x = 0~10%) lead-free piezoelectric ceramics have been synthesized by using the conventional mixed oxide process and electronic grade raw materials. The crystalline phase, microstructure and electric properties of the ceramics were studied. When x ≤ 4%, the ceramics with perovskite structure possesses the orthorhombic phase, and when x ≥ 6%, a second phase of K3Li2Nb5O15 with tetragonal tungsten bronze structure appears. With LiNbOE amount increasing, the phase transition temperature (TO-T) of orthorhombic to tetragonal is shifted to the lower temperatures while the Curie temperature TC is shifted to the higher temperatures in the dielectric constant-temperature curves. At x = 4%, the optimal electric properties were obtained: piezoelectric constant d33 = 116 pC/N, planar electromechanical coupling factor kp = 40.6%, remanent polarization Pr = 21.0 μC/cm2, coercive filed Ec = 0.96 kV/mm, and the Curie temperature Tc = 452°C respectively. The results show that KNN + xLN is a good candidate for lead-free piezo-and ferroelectric ceramics for a wide range of temperature application because of their larger planer electromechanical coupling coefficient and higher Curie temperature.