Magnetic Properties of a Bottom‐Up Synthesis Analogous Graphene with N‐Doped Zigzag Edges
Jie Xu,Weifeng Zhang,Dechao Geng,Yuan Liu,Huaping Wang,Nujiang Tang,Gui Yu
DOI: https://doi.org/10.1002/aelm.201500084
IF: 6.2
2015-01-01
Advanced Electronic Materials
Abstract:DOI: 10.1002/aelm.201500084 magnetic moment. [ 30 ] However, it is diffi cult to experimentally clarify the specifi c contribution by each specifi c type of N types in N-doped graphene due to uncertain confi guration. [ 12,27 ] The exact contribution mechanism needs to be confi rmed by more experimental works. Therefore, it is urgent and important to construct graphene derivatives with specifi c chemical confi guration in order to make clear the magnetic source of graphenebased materials. It is a tempting target to construct π-conjugated twodimensional (2D) well-organized molecules with specifi c physical and chemical properties by elaborately controlling both atomic composition and structure with different edges, since such skeletons have potential in various applications. [ 31,32 ] For example, the conjugated 2D material from the condensation of a carbazole derivative exhibits blue luminescence. [ 33 ] The conjugated 2D structure based on the condensation reaction of triphenylene and pyrene monomers is electrically conductive and capable of reduplicative on–off current switching at room temperature. [ 34 ] However, as far as we know, exploring the magnetic properties of π-conjugated 2D molecules has not been realized experimentally. Therefore, it is important and useful to construct a π-conjugated 2D structure with specifi c chemical confi guration for exploring the magnetic properties and magnetic source of carbon-based materials. Furthermore in theory, pyridinic N at the zigzag edges is confi rmed to be magnetic, regardless of whether the edges are regular or irregular, and creates a magnetic moment of 0.32 μ B . [ 12,14 ] The extended structures of hexaazatriphenylene were denoted HATs ( Scheme 1 , HATs), which belong to one of π-conjugated 2D molecules in this communication. In this contribution, we have studied the magnetic properties from the controlled introduction of specifi c type nitrogen doped on analogous graphene skeleton with zigzag edges. HATs, which are π-conjugated 2D well-organized molecules with analogous graphene with N-doped zigzag edges skeleton, were prepared by a condensation reaction of 1,2,4,5-benzenetetramine with triquinoyl hydrate at different conditions. Our experimental results revealed that producing analogous larger graphene skeleton with pyridinic N-doped zigzag edges can improve the magnetization. HAT-180 from the optimal preparation condition exhibited a relatively high magnetization of 0.609 emu g −1 and high localized spin magnetic moment of 9.5 μ B per 1000 N atoms. Finally, and most importantly, highly sensitive technique of Inductively Coupled Plasma Optical Emission Spectroscopy (ICP-OES) in HATs was carried out, and the contents of metal impurity elements were negligible below 1 ppm. This indicated that metal impurity species possibly introduced by the synthesis procedures have been removed, cannot affect the magnetic properties, and lead to misinterpretation. The magnetism of carbon-based materials as light nonmetallic magnets has been the emerging concentration. [ 1–3 ] Especially, magnetism of graphene is of particular interest due to the light weight magnets and the long spin diffusion lengths, which result from the weak spin-orbit and hyperfi ne interactions. The nature could lead graphene to be an outstanding material for spintronics and other memory-based device applications which vouchsafe information storage, handling, and fl ow at faster speeds with lower power consumption. [ 4–8 ] However, pristine graphene is usually nonmagnetic and absence of localized magnetic moments due to a delocalized π-bonding network, which hinders its applications in spintronic and other memory based devices. Theoretically, localized magnetic moments in graphene by the formation of unpaired spins can be induced by defects such as vacancies, foreign atoms, and zigzag edges, etc. [ 9–15 ]