Construction and ectopic osteogenesis of chitosan-calcium phosphate/human bone morphogenetic protein-2 composite materials in vivo
Liang Hong,Zhi-zhong Li,Jing Wang,Yong-xin Lin,Ying Tan,Gen-long Jiao,Bo-Wen Wu,Wen-quan Wang,Ke-yun He,Guo-dong Sun
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.49.003
2008-01-01
Abstract:Background: It has been demonstrated that chitosan and calcium phosphate cement with human bone morphogenetic protein-2 (rhBMP-2) has good cell compatibility, which more suitable for the cell growth and bone regeneration for its porous structure and pore diameter. However, whether the composite materials can osteogenesis in vivo needs further study. Objective: To construct the chitosan-calcium phosphate/rhBMP-2 composite materials, further more, to observe the ectopic osteogenesis of the composite materials after implanting it into rabbit muscular tissue. Design, time and setting: The observational experiment was performed at the Central Laboratory and Surgical Laboratory of the First Affiliated Hospital of Jinan University and the Laboratory of Materials Science and Engineering, Jinan University Technology College from June to August in 2007. Materials: The scaffold of chitosan-calcium phosphate cement was produced and taken into rhBMP-2 solution, followed by vacuum aspiration and freeze-drying to harvest the chitosan-calcium phosphate/rhBMP-2 composite materials. Methods: The porosity and compressive strength of chitosan-calcium phosphate/rhBMP-2 composite materials were measured, and its microstructure was observed via scanning electron microscopy. A total of 20 New Zealand rabbits were divided into the blank control (n=5), pure chitosan-calcium phosphate (n=5) and composite materials (n=10) groups. The scaffolds were implanted intramuscularly. There was no treatment in the blank control group except exposed the muscle of upper leg. Main outcome measures: The gross observation, X-ray films, as well as histological examination were used to measure the ectopic ossification and biological response after 4 weeks of implantation. Results: The porosity of rhBMP-2/chitosan-calcium phosphate composite scaffold was 87%, with compressive elastic modulus of 20 MPa. The scanning electron microscope showed that there was interconnected pore structure, which over 100 μm in diameter in the material. In the blank control group, hematoxylin-eosin staining showed that there was sparse lymphocytic infiltration around muscle fibers. In the pure chitosan-calcium phosphate group, the gross observation demonstrated that the materials were encapsulated by connective tissues, the connection between material mad muscle was loose, and there was circular cavity in the implanted area. In the composite materials group, the scaffold was encapsulated by connective tissues, with cavity in the middle, and fibriform structure decomposed into the scaffold. The X-ray revealed that the high density shadow was not obvious changes. Hematoxylin-eosin staining and Masson displayed that connective tissue involving blood vessels and collagen fibers formed in the woven bone islands. Conclusion: The chitosan-calcium phosphate/rhBMP-2 composite materials is three-dimensional, porous with good compression strength, which has ability of ectopic osteogenesis in rabbits.