Biomechanic characteristics and adhesion performance of bovine acellular bone matrix

Xiao-lei Sun,Xin-long Ma,Jian-xiong Ma,Tao Zhang,Zhi-gang Wang,Tao Wang,Hua-feng Zhang

DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.49.023

2008-01-01

Abstract:Background: Acellular bone matrix has a special advantage as a kind of bone-derived materials used in bone tissue engineering scaffold. Objective: To study the biomechanics characteristics, interval porosity and adhesion performance of bovine acellular bone matrix (BABM), additionally, to investigate the feasibility as a natural scaffold of bone tissue engineering. Design, time and setting: The mechanical load test used randomized controlled observation, was performed at the Laboratory of Orthopaedics, General Hospital of Tianjin Medical University from February to June 2008. Materials: Fresh bovine femoral bone was harvested from male, Mongolian cattle with 16 months, weighing 350 kg, and three neonatal SD rats. Methods: The BABM was prepared by the method of 100 g/L NaCl combined with 1% TritonX-100. The BABM was dislodged, decalcification and cut into slices. The mechanical equipment ElectroForce3200 was used to perform mechanical load test to the specimens. The 3rd passages of osteoblast cultured form neonatal SD rats were co-cultured with BABM in vitro for 12 hours. The control group was cultured with 9 g/L NaCl solution. Main outcome measures: The mean pore diameter and interval porosity of the BABM, the elastic strength, destroy load and elastic modulus as well as the adhesive rate were detected by hematoxylin-eosin staining and flow cytometry, respectively. Results: 1 The method of 10% NaCl combined with 1% TritonX-100 could completely remove the cell components of the BABM, which had no significant damage to bone trabecula compared with the control group. 2 The diameter of the BABM was (376.3 ± 80.9) μ m, with the porosity of (70.15 ± 2.98)%. 3 The mechanical testing showed that no significant effect on mechanical properties of the BABM by the method of 10% NaCl combined with TritonX-100. 4 The BABM had satisfactory adhesion performance with osteoblast cultured in vitro, the adhesion rate was 62.38%. Conclusion: The BABM is an ideal natural scaffold material, which has satisfactory mechanical properties and the closest to the physical structure in diameter and porosity, can meet the requirements of adhesion properties as bone tissue engineering scaffold.