Abstract:BACKGROUND: Hydroxyapatite exhibits slow degradation and great fragility, while silk fibroin is weak in the mechanical strength, so the combination of the two will benefit to overcome their own shortcomings. OBJECTIVE: To test the water absorption rate and degradation rate in vivo of silk fibroin/hydroxyapatite (SF/HA) composite, so as to provide evidences for further study on the bone formation of SF/HA. DESIGN, TIME AND SETTING: A randomized and controlled experimental study was carried out in the Laboratory of Orthopaedics Department, the First Affiliated Hospital of Soochow University from September 2006 to Jun 2007. MATERIALS: Four kinds of SF/HA-1, SF/HA-2, SF/HA-3, SF/HA-4 and common HA. They varied each other with the component ratio of SK/HA, pore-forming dosage and additives' dosage. METHODS: The water absorption rate of 4 types of SF/HA composites and HA were measured at 0.5, 2, 6, 12 and 24 hours after these materials soaked in deionized water. Four SF/HA composites were implanted into SD rats' back subcutaneously to observe their degradation rate in vivo. MAIN OUTCOME MEASURES: The water absorption rate of all materials was measured; and the degradation of these materials were evaluated by gross observation and histological examination in SD rats. RESULTS: Water absorption rates in 4 kinds of SF/HA composites were as follows: SF/HA-3 and SF/HA-4>SF/HA-2 and SF/HA-1>HA. HA, SF/HA-1 and SF/HA-2 had little degradation. SF/HA-3 had complete degradation in 20-24 weeks after operation, while SF/HA-4 had complete degradation in 12-16 weeks. Tissue surrounding all materials had no apomorphosis or necrosis. CONCLUSION: SF can improve physical and chemical properties of HA, and change the bio-degradation rate of SF/HA. The composite of SF/HA has a good histocompatibility, and may be suitable for bone tissue engineering scaffold.

Water absorption rate of silk fibroin/hydroxyapatite composite and its degradation in SD rats

Preparation and characterization of nano-hydroxyapatite/silk fibroin porous scaffolds.

Preparation and Performance of Silk Sericin/Hydroxyapatite Composite Bone Scaffold

Characterization and Cytocompatibility of Premineralized Silk Fibroin/Chitosan Composite Scaffolds

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

Effects of Different Structure Silk Fibroin on Crystallization of Hydroxyapatite

Cell Biocompatibility of Hydroxyapatite/Silk Fibroin Composite Scaffolds Carrying Bone Morphogenetic Protein

Study on Porous Silk Fibroin/ hydroxyapatite Composites Used as Bone Defect Treatment

Preparation and Characterization of the Silk Fibroin/hydroxyapatite Composites

High-affinity Integration of Hydroxyapatite Nanoparticles with Chemically Modified Silk Fibroin

Silk Fibroin Regulates Osteoconduction of Hydroxyapatite in Rat Spine Fusion Model

Enhanced Silk Fibroin/Sericin Composite Film: Preparation, Mechanical Properties and Mineralization Activity

Study on Tissue Engineering Scaffolds of Silk Fibroin-Chitosan/Nano-Hydroxyapatite Composite

Microstructure and Gelation Behavior of Hydroxyapatite-Based Nanocomposite Sol Containing Chemically Modified Silk Fibroin

Silk Fibroin-Alginate-Hydroxyapatite Composite Particles in Bone Tissue Engineering Applications In Vivo

Silk fibroin/hydroxyapatite scaffold: a highly compatible material for bone regeneration

Preparation and Properties on Silk Fibers Reinforced Hydroxyapatite/Chitosan Composites

The Cellular Compatibility and the Ectopic Bone Formation of Silk Fibroin/hydroxyapatite

Effect of silk fibroin on degradation and in vivo biocompatibility of poly (L-lactic-co-ε-caprolactone)electronspun nanofibrous scaffolds

The Comparative of the Cytocompatibility of Silk Fibroin and Silk Fibroin/Hydroxyapatite Composites

Support of silk fibroin/hydroxyapatite scaffold on the proliferation and differentiation of bone marrow mesenchymal stem cells: Superior to collagen sponge?