Abstract:Effect of hydrogen on deformation behavior of the Ti-6Al-4V alloy was investigated through isothermal compression.Addition of hydrogen decreases significantly flow stress,improves strain rate of more than one order of magnitude and decreases significantly deformation temperature of the Ti-6Al-4V alloy.The minimum flow stress of Ti-6Al-4V alloy is at a hydrogen content of 0.4wt% in the deformation temperature range from 760℃ to 800℃,but the minimum flow stress is at a hydrogen content of 0.2wt% in the deformation temperature range from 840℃ to 920℃.Meanwhile,apparent activation energy for deformation of the Ti-6Al-4V alloy is 208.3kJ/mol at a hydrogen content of 0.4wt% in α+β two-phase field,decreasing 316kJ/mol in comparison with that of the Ti-6Al-4V alloy with natural hydrogen.

Deformation Behavior in the Isothermal Compression of Hydrogenated Ti-6Al-4V Alloy