Green waterborne synthesis of hemocompatible polycarbonate–polyether polyurethanes
Dean-Jay Wang,Shan-hui Hsu
DOI: https://doi.org/10.1016/j.mtcomm.2024.109351
IF: 3.8
2024-06-01
Materials Today Communications
Abstract:Polyurethane (PU) is a family of biomedical elastomers with promising applications. In this study, we describe the synthesis of a novel waterborne PU with high solid content and low viscosity. The soft segment of the PU consists of polycarbonate diol (PCDL) and polytetramethylene ether glycol. Dimethylolbutanoic acid is used as a chain extender. To stabilize the emulsion in the synthetic process, nonionic groups (polyoxyethylene styrenated phenyl and polyoxyethylene tridecyl ethers) are used as surfactants. PUs with good hydrophilicity and proper hemocompatibility were successfully synthesized using this approach. The chemical composition of the PU was adjusted by changing the soft-to-hard segment ratio. The effects of this composition ratio on the crystallization properties of PU were characterized using differential scanning calorimetry, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, attenuated total reflectance infrared spectroscopy, thermogravimetric analysis, alternating magnetic field, and contact angle measurements. Film casts from PUs prepared in this study showed good mechanical properties, including Young's modulus (0.66–48 MPa), tensile strength (11.7–30.9 MPa), and strain at break (173%–579%). Moreover, introducing PCDL in the soft segment during preparation improved the microphase separation and reduced the water contact angle of the films, which enhanced the hydrophilicity of the PU. Our findings demonstrate the potential of the new waterborne PU formulation to significantly improve the performance and durability of biomaterials and blood-contacting devices. Furthermore, this formulation meets the required hemolytic standards, which supports its suitability for medical applications.
materials science, multidisciplinary