Magnetic properties of Cr/Gd/Cr film at low temperatures

Zhiwei Jiao,WeiDi Jiang,Jie Gong,Gaoxiang Ye

DOI: https://doi.org/10.3321/j.issn:1002-185x.2008.09.016

2008-01-01

Rare Metal Materials and Engineering

Abstract:The Cr/Gd/Cr films were deposited on glass substrate by DC magnetron sputtering method. The microstructure and magnetic properties of the films were characterized by means of X-ray diffraction (XRD) and Vibrating-sample magnetometer (VSM). It was shown that the Curie temperature T-C (297 K) of the film is higher than the T-C (293 K) of the bulk Gd. It was observed that the spins of the ferromagnetic Gd layer exchange with the spins of the antiferromagnetic Cr layer at the interface by ferromagnetic couple. The temperature dependence of coercivity and exchange bias field exhibit normal behaviors at the temperature ranges of 80 similar to 200 K and 250 similar to 290 K; however, the exchange bias field decreases and the coercivity increases anomalously with the increase of temperature, respectively, at the temperature range of 200 similar to 250 K, which is due to the fact that the direction of the spontaneous moment of Gd varies with the temperature and leads to the decrease of the exchange interaction between the Gd and Cr.