Abstract:Multiferroic Bi1−xLaxFeO3 [BLFO (x)] ceramics with x = 0.10–0.50 and Mn‐doped BLFO (x = 0.30) ceramics with different doping contents (0.1–1.0 mol%) were prepared by solid‐state reaction method. They were crystallized in a perovskite phase with rhombohedral symmetry. In the BLFO (x) system, a composition (x)‐driven structural transformation (R3c→C222) was observed at x = 0.30. The formation of Bi2Fe4O9 impure phase was effectively suppressed with increasing the x value, and the rhombohedral distortion in the BLFO ceramics was decreased, leading to some Raman active modes disappeared. A significant red frequency shift (~13 cm−1) of the Raman mode of 232 cm−1 in the BLFO ceramics was observed, which strongly perceived a significant destabilization in the octahedral oxygen chains, and in turn affected the local FeO6 octahedral environment. In the Mn‐doped BLFO (x = 0.30) ceramics, the intensity of the Raman mode near 628 cm−1 was increased with increasing the Mn‐doping content, which was resulted from an enhanced local Jahn–Teller distortions of the (Mn,Fe)O6 octahedra. Electron microscopy images revealed some changes in the ceramic grain sizes and their morphologies in the Mn‐doped samples at different contents. Wedge‐shaped 71° ferroelectric domains with domain walls lying on the {110} planes were observed in the BLFO (x = 0.30) ceramics, whereas in the 1.0 mol% Mn‐doped BLFO (x = 0.30) samples, 71° ferroelectric domains exhibited a parallel band‐shaped morphology with average domain width of 95 nm. Dielectric studies revealed that high dielectric loss of the BLFO (x = 0.30) ceramics was drastically reduced from 0.8 to 0.01 (measured @ 104 Hz) via 1.0 mol% Mn‐doping. The underlying mechanisms can be understood by a charge disproportion between the Mn4+ and Fe2+ in the Mn‐doped samples, where a reaction of Mn4+ + Fe2+→Mn3+ + Fe3+ is taken place, resulting in the reduction in the oxygen vacancies and a suppression of the electron hopping from Fe3+ to Fe2+ ions effectively.

Ferroic Properties of Highly Dense Multiferroic Bi1-Xla0.05tbxfeo3 Ceramics Via Sheltered Spark Plasma Sintering

Ferroelectric and Ferromagnetic Properties of Hot‐Pressed Bi0.95−xLa0.05TbxFeO3 Ceramics

Multiferroic Properties of Bi0.87La0.05Tb0.08FeO3 Ceramics Prepared by Spark Plasma Sintering

Preparation, Structures, And Multiferroic Properties Of Single Phase Bi1-Xlaxfeo3 (X=0-0.40) Ceramics

Simultaneously Enhanced Ferroelectric and Magnetic Properties in Fe-substituted Ba4Sm2Fe Ti4-2Nb6+O30 Ceramics

Multiferroic Properties of (1 −X)[0.94bi0.5na0.5tio3–0.06batio3]–xcofe2o4ceramics

Composition Designing and Sintering Behavior Tailoring in [(ba1−xcax)0.995eu0.005](ti1−yhfy)o3 Multifunctional Piezoceramics

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

Preparation Of Fine-Grained Multiferroic Batio3-(Ni0.5zn0.5) Fe2o4 Ceramic Composites

Enhanced Ferroelectric Properties In Bi0.86sm0.14feo3-Based Ceramics

Multiferroic Properties of Single-Phase Bi0.85la0.15feo3 Lead-Free Ceramics

Structural, Raman, and Dielectric Studies on Multiferroic Mn‐doped Bi1−xLaxFeO3 Ceramics

Substitution-Induced Phase Transition And Enhanced Multiferroic Properties Of Bi1-Xlaxfeo3 Ceramics

High-Temperature Ferroelectric Phase Transition Observed in Multiferroic Bi0.91la0.05tb0.04feo3

Enhancing Energy Storage Performance of 0.85Bi0.5Na0.5TiO3-0.15LaFeO3 Lead-Free Ferroelectric Ceramics via Buried Sintering

The evolution of structure, properties and polar domains in rare earth and PbTiO3 co-substituted BiFeO3 ferroelectric ceramics

Dielectric, impedance, and ferroelectric performances with structural heterogeneity of Sr0.7Bi0.2TiO3 modified lead-free bismuth ferrite-based ceramics

Optimizing Structural, Optical, Dielectric, and Magnetic Properties of (Bi1- x La x )FeO3 (0.00 ≤ x ≤ 0.06) Sintered Ceramics

Short communicationMultiferroic properties of Bi0.8La0.2FeO3/CoFe2O4 multilayer thin films

Processing And Ferroelectric Properties Of Ti-Doped Bifeo3 Ceramics

Impedance Spectroscopy of Fe and La-Doped BaTiO3 Ceramics