Abstract:A series of Tb3+-doped Sr2YTaO6 double perovskite phosphors (SYT:Tb3+) were synthesized using a conventional solid-state reaction method. A strong green emission was observed in the SYT:Tb3+ phosphors, and the optimal doping concentration of Tb3+ was confirmed to be 5 mol%. The electric dipole-dipole interaction was ascribed to be the main mechanism for the luminescence concentration quenching. Analysis of the concentration-dependent fluorescence decay confirmed that the self-generated quenching model holds for the dynamic process of Tb3+ decays in SYT. Furthermore, the internal quantum efficiencies, non-radiative transition rates, and energy transfer rates of the 5D4 level for the SYT:Tb3+ samples were estimated, respectively. The luminescence thermal stability of the sample was also evaluated based on the Arrhenius model. The chromaticity shift of the SYT:5 mol% Tb3+ phosphor was examined to be 0.013 when the sample temperature was increased from 303 to 483 K, thus indicating excellent chromaticity shifting resistance under high temperature conditions. Moreover, the Judd-Ofelt parameters were calculated from the emission spectra of SYT:Tb3+ to be Ω2 = 0.29 × 10-20, Ω4 = 0.45 × 10-20, and Ω6 = 0.72 × 10-20 cm2, respectively. The fluorescence branching ratios and radiative transition rates for the 5D4 level were calculated based on the obtained Judd-Ofelt parameters. Finally, a white light-emitting diode (LED) prototype was assembled using a 310 nm LED chip combined with a prepared green SYT:Tb3+ phosphor and two other commercial blue and red phosphors. The obtained warm white light exhibits good chromaticity coordinates (0.32, 0.32) and a high color rendering index of 96.1. Based on the above results, it can be known that the prepared SYT:Tb3+ phosphors have a potential application as green emitting phosphors in white LEDs.

Luminescence properties of Ce3+ and Tb3+ ions codoped strontium borate phosphate phosphors

Luminescence Properties And Energy Transfer Of Ce3+,Tb3+-Coactivated-Sialon Phosphors

Preparation and luminescence properties of Ce3+ and Tb 3+ co-doped glasses and glass ceramics containing SrF2 nanocrystals

Color point tuning for Ce3+ and Tb3+ activated Sr5(BO3)3F phosphors

Photoluminescence properties, excellent thermal stability and energy transfer in Ce3+ and Tb3+ co-doped Sr3Gd2(BO3)4 phosphors

[Synthesis and fluorescence properties of SrZn(WO4)2:Tb3+, Ce3+ phosphors]

Luminescence and energy transfer of Ce3+/Tb3+ activated fluoroborate BaGaBO3F2 as a color tunable phosphor

Novel Luminescence Behaviors of Ce3+/Tb3+ Co-Doped Phosphate Glasses

Synthesis and luminescence properties of Sr3MgSi2O8:Ce3+,Tb3+ for application in near ultraviolet excitable white light-emitting-diodes

Photoluminescence Properties and Energy Transfer in Color Tunable BaY2Si3O10:Ce,Tb Phosphors

Enhanced Green Luminescence and Energy Transfer Studies in Ce3+/Tb3+-codoped Α-Zirconium Phosphate Nanosheet

Investigation of Luminescence of La(BO3,PO4):Ce,Tb,Gd

Highly Efficient Green-Emitting Phosphors Ba2Y5B5O17 with Low Thermal Quenching Due to Fast Energy Transfer from Ce3+ to Tb3

Luminescent properties and energy transfer mechanism from Tb3+ to Eu3+ in color adjustable nano Ca5(PO4)3(OH): Eu3+,Tb3+ phosphors

Ce3+/Tb3+ Co-Doped Kbay(Bo3)(2): A Color-Tunable Blue-Green Phosphor for Near-Uv White Leds

Photoluminescence Properties and Energy Transfer of a Novel Bluish-Green Tunable KSrY(PO4)2:Ce3+, Tb3+ Phosphor

Preparation and Photoluminescence of the Ce-, Tb- and Gd-doped Lanthanum Borophosphate Phosphor

Energy transfer, optical properties and thermal stability of Ce3+, Tb3+ activated apatite-type Ca8NaGd(PO4)6F2 phosphors

Synthesis, Structure, and Photoluminescence Properties of Ce3+ and Tb3+ Doped Alkaline-Earth Silicate Sr2mgsi2o7 Phosphors for Wleds

Excitation wavelength and Eu3+/Tb3+ content ratio dependent tunable photoluminescence from NaSrBO3:Eu3+/Tb3+ phosphor

Luminescence properties and Judd-Ofelt analysis of Tb3+ doped Sr2YTaO6 double perovskite phosphors for white LED applications