LI Xue,LI Jin-hua,FANG Xuan,WEI Zhi-peng,WANG Xiao-hua
2008-01-01
Chinese Journal of Luminescence
Abstract:We configured reaction solution using zinc acetate [Zn(CH3COO)2 ·2H2O]and methenamine (C6H12N4) with a certain percentage,magnesium acetate [Mg(CH3COO)2·4H2O]was added appropriately in the reaction solution. High quality ZnO microrods were prepared on the silicon substrate at 90 ℃ for 24 h by hydrothermal method. Surface morphology and crystal structure of ZnO microrods are analyzed,using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show the sample presents a rod-like shape with a hexagonal cross sections and typical morphology of wurtzite ZnO. The ratio of length and diameter of the ZnO rod is about 10∶1. And the ZnO microrods grow along [002]direction. Mg ions are not found in the sample,which probably played the role of a catalyst. Photoluminescence (PL) spectrum of ZnO microrods was measured. Room-temperature PL spectrum of the sample shows an UV luminescence peak located at 384 nm,and the FWHM of the emission peak is only 13 nm,intensity of UV luminescence peak is stronger than that of visible luminescence peak,indicating the high quality of the sample.
What problem does this paper attempt to address?