Abstract:BACKGROUND: Corneal blindness resulting from various medical conditions affects millions worldwide. The rapid developing tissue engineering field offers design of a scaffold with mechanical properties and transparency similar to that of the natural cornea. AIM: The present study aimed at to prepare and investigate the properties of PVA/chitosan blended scaffold by further cross-linking with 1-Ethyl-3-(3-dimethyl aminopropyl)-carbodiimide (EDC) and 2 N-Hydroxysuccinimide (NHS) as potential in vitro carrier for human limbal stem cells delivery. MATERIAL AND METHODS: Acetic acid dissolved chitosan was added to PVA solution, uniformly mixed with a homogenizer until the mixture was in a colloidal state, followed by H2SO4 and formaldehyde added and the sample was allowed to cool, subsequently it was poured into a tube and heated in an oven at 60°C for 50 minutes. Finally, samples were soaked in a cross-linking bath with EDC, NHS and NaOH in H2O/EtOH for 24 h consecutively stirred to cross-link the polymeric chains, reduce degradation. After soaking in the bath, the samples were carefully washed with 2% glycine aqueous solution several times to remove the remaining amount of cross-linkers, followed by washed with water to remove residual agents. Later the cross-linked scaffold subjected for various characterization and biological experiments. RESULTS: After viscosity measurement, the scaffold was observed by Fourier transform infrared (FT-IR). The water absorbency of PVA/Chitosan was increased 361% by swelling. Compression testing demonstrated that by increasing the amount of chitosan, the strength of the scaffold could be increased to 16×10−1 MPa. Our degradation results revealed by mass loss using equation shows that scaffold degraded gradually imply slow degradation. In vitro tests showed good cell proliferation and growth in the scaffold. Our assay results confirmed that the membrane could increase the cells adhesion and growth on the substrate. CONCLUSION: Hence, we strongly believe the use of this improved PVA/chitosan scaffold has potential to cut down the disadvantages of the human amniotic membrane (HAM) for corneal epithelium in ocular surface surgery and greater mechanical strength in future after successful experimentation with clinical trials.

Porous Nano-Hydroxyapatite/Poly(Vinyl Alcohol) Composite Hydrogel As Artificial Cornea Fringe: Characterization and Evaluation in Vitro

Active loading graphite/hydroxyapatite into the stable hydroxyethyl cellulose scaffold nanofibers for artificial cornea application

Preparation and Evaluation of Bacterial Nanocellulose/Hyaluronic Acid Composite Artificial Cornea for Application of Corneal Transplantation

Grafting with Chondroitin Sulfate on Poly(vinyl Alcohol) to Improve Antifouling Property

Preparation and characterization of nano-hydroxyapatite/poly(vinyl alcohol) hydrogel biocomposite

Design and fabrication of an artificial cornea based on a photolithographically patterned hydrogel construct

Chitosan-functionalized silk fibroin 3D scaffold for keratocyte culture

Enhanced biocompatibility of PLGA nanofibers with gelatin/nano-hydroxyapatite bone biomimetics incorporation.

Study on biocompatibility of complexes of collagen-chitosan-sodium hyaluronate and cornea.

Photocrosslinked methacrylated poly(vinyl alcohol)/hydroxyapatite nanocomposite hydrogels with enhanced mechanical strength and cell adhesion

A Core-Skirt Designed Artificial Cornea with Orthogonal Microfiber Grid Scaffold.

Biomimetic bone-like composites as osteo-odonto-keratoprosthesis skirt substitutes

Introducing Antifouling Properties Onto Janus‐Like Decellularized Corneas via Graft‐From Zwitterionic Polymers

Evaluation of an Improved Chitosan Scaffold Cross-Linked With Polyvinyl Alcohol and Amine Coupling Through 1-Ethyl-3-(3-Dimethyl Aminopropyl)-Carbodiimide (EDC) and 2 N-Hydroxysuccinimide (NHS) for Corneal Applications

Preclinical evaluation of the safety and effectiveness of a new bioartificial cornea

Engineering of Corneal Tissue Through an Aligned PVA/Collagen Composite Nanofibrous Electrospun Scaffold.

Mimicking the Physicochemical Properties of the Cornea: A Low-Cost Approximation Using Highly Available Biopolymers

Biodegradable-Glass-Fiber Reinforced Hydrogel Composite with Enhanced Mechanical Performance and Cell Proliferation for Potential Cartilage Repair

Design and Biocompatibility of a Novel, Flexible Artificial Cornea

Preparation and In Vitro Characterization of Gelatin Methacrylate for Corneal Tissue Engineering

In Vivo Study of the Biocompatibility of a Novel Compressed Collagen Hydrogel Scaffold for Artificial Corneas.