Influence of Substrate Thermal Conductivity on the Phase Composition of High Velocity Oxy-Fuel Sprayed Al-Cu-Cr Quasicrystalline Coatings

FU Ying-qing,REN Zhong-xing,LIANG Zhi-qiang,ZHOU Feng,GAO Yang
DOI: https://doi.org/10.16411/j.cnki.issn1006-7736.2008.01.009
2008-01-01
Abstract:Al-Cu-Cr quasicrystalline coatings were prepared on AISI304,45 steel,Al and Cu substrates respectively using identical high velocity oxy-fuel(HVOF) spray parameters to investigate the influence of substrate thermal conductivity on the phase composition of the coatings.X-ray diffraction(XRD) results show that the feedstock powders consist of a dominant icosahedral quasicrystalline phase I-Al65Cu24Cr11 and a minor monoclinic crystalline phase θ-Al13Cr2(i.e.Al83Cu4Cr13).However,besides these two phases,an approximant to I-Al65Cu24Cr11, α-Al69Cu18Cr13(body-centered cubic) was detected in all coatings.The phase assemblage of the as-sprayed coatings was affected significantly by substrate thermal conductivity.The XRD α/I and θ/I peak intensity ratios increase with the substrate thermal conductivity rising.The amount of I in the coating deposited on AISI304 substrate is larger than that on Cu,but the amount of α and θ is less than the latter.
What problem does this paper attempt to address?