Abstract:Straight and branched carbon nanotubes (CNTs) were synthesized by catalytic chemical pyrolysis through jet sample introduction. And using them as carriers, different nano-NiO/CNTs composites were prepared by chemical precipitation. Further research on the catalysis of the thermal decomposition of ammonium perchlorate (AP) by. single particles, combined particles and composite particles was carried out and the difference of the catalysis was also discussed. The results show that the straight-CNTs with good morphology, lesser defects and better degree of graphitization and the branched-CNTs with high contents of branched structures, more defects and worse degree of graphitization could be controlled by the experimental conditions. The synthesized NiO/CNTs composites with good crystallinity, uniform coats and large surface area had good catalysis on the thermal decomposition of AP. Between the two composites, the catalysis by NiO/branched-CNTs was better and they decreased the high temperature decomposition peak of AP by 94.6 degrees C and increased the apparent heat of decomposition of AP by 819 J center dot g(-1), respectively. The supporting effect of the CNTs could effectively prevent the aggregation of particles, and increase the specific surface area and the active sites. The branch structure of CNTs was propitious to improve the catalysis of the NiO/branched-CNTs composites.

Preparation of Monodispersed Co Nanoparticles and Its Effect on the Thermal Decomposition of Ammonium Dinitramide

PREPARATION OF NANOMETER Ni AND AMORPHOUS Ni-B ALLOYS AND THEIR EFFECTS ON THE THERMAL DECOMPOSITION CHARACTERISTICS OF AMMONIUM PERCHLORATE

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

Preparation and magnetic properties of nickel nanoparticles via the thermal decomposition of nickel organometallic precursor in alkylamines

Catalytic Performance of Nanometer Co-B Amorphous Alloy for Ammonium Perchlorate Decomposition

Synthesis of Ni Nanoparticles and Their Catalytic Effect on the Decomposition of Ammonium Perchlorate

Study on the Preparation and Catalytic Characteristics of Nano-Nickel Powder

Preparation of G-C3 N4/NiO Composites and Its Effect on T Hermal Decomposition of Ammonium Perchlorate

Synthesis of Core-Shell Metal Powders and Catalytic Effect on the Decomposition of Ammonium Perchlorate (Ap)

Effects of nano NiO/CNTs and Co_3O_4/CNTs on thermal decomposition of AP and HTPB / AP propellant

A Combined Experimental and Theoretical Study of the Thermal Decomposition Mechanism and Kinetics of Ammonium Dinitramide (ADN)

Preparation of Nanocrystalline Co3O4 and Its Catalytic Performance for Thermal Decomposition of Ammonium Perchlorate

Effect of Amorphous Alloy CoB Nanoparticles on the Decomposition of Ammonium Perchlorate

Synthesis and Catalytic Properties of NiCu Composite Metal Nanopowder

Catalysis of Nanometer Transition Metals on the Thermal Decomposition of Ammonium Perchlorate

Preparation and Thermal Decomposition Behavior of Nano-Nd2O3/Ammonium Perchlorate Composite Particles

Study on preparation and catalytic properties of Co-B hollow nanospheres

Preparation of Nanometer NiO/MgO and Its Catalytic Performance for Thermal Decomposition of Ammonium Perchlorate

PREPARATION OF NANOMETER SIZE α-Fe2O3 AND ITS CATALYSIS ON THE THERMAL DECOMPOSITION OF AMMONIUM PERCHLORATE

Nano-NiO/straight-CNTs and Nano-NiO/branched-CNTs composites and their effects on the thermal decomposition of ammonium perchlorate

Preparation of Co3O4/CNTs Composites and Their Catalytic Effects on the Thermal Decomposition of AP and AP/HTPB Propellant