Abstract:Novel Ti/PbO2-Cr-PEDOT electrodes were prepared by electrodeposition for electrochemical degradation of phenolic wastewater. The electrodes were characterized by XRD, SEM-EDS, XPS, and FT-IR to study the crystalline, surface morphology, elements distribution, and microstructure of the electrodes. A flat and compact interface was obtained with Cr and PEDOT doping into beta-PbO2 plate by electrodeposition method. The linear sweep voltammetry (LSV) and electrochemical impedance spectroscopy (EIS) were conducted to explore the electrochemical performance of the prepared electrodes. The Ti/PbO2-Cr-PEDOT electrode exhibited a higher oxygen evolution potential (OEP, 2.53 V vs SCE) and a lower charge transfer resistance compared with Ti/PbO2. Phenol degradation efficiency of 100% and TOC removal rate of 95.02% were achieved in the electrochemical degradation of phenol within 120 min. The optimal process parameters (phenol concentration = 1000 mg.L-1, electrolyte concentration = 4.0 g.L-1, current density = 15 mA.cm(-2) and electrode distance = 3 cm) in the process of electrochemical oxidation of phenol wastewater were explored. Active species trapping experiments proved that center dot OH radicals played an important role in the electrochemical system. Furthermore, the electrode also showed high activity for the degradation of other phenolic wastewaters such as phloroglucinol (eta(DEP) = 100%), bisphenol A (eta(DEP) = 97.17%) and p-chlorophenol (eta(DEP) = 89.77%) within 60 min. A possible degradation pathway was proposed based on the intermediate products determined by HPCL. The Ti/PbO2-Cr-PEDOT electrode showed excellent stability with only 3% loss of degradation efficiency (eta(DEP )= 96.95%) after recycling tests for 5 times. These results suggest that Ti/PbO2-Cr-PEDOT is a promising electrode for electrochemical degradation of phenolic wastewaters.

Degradation of dye wastewater using a rotating TiO2/Ti disc photoanode

Advances in Photocatalytic Degradation of Dyestuffs with TiO2

Phenol Degradation by TiO2 Photocatalysts Combined with Different Pulsed Discharge Systems.

Photocatalytic Membrane Reactor for Degradation of Acid Red B Wastewater

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

In situ recombination for durable photoelectrocatalytic degradation of organic dye in wastewater

Fabrication of Fe2O3/TiO2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Fabrication of Fe 2 O 3 /TiO 2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation: Fabrication of Fe 2 O 3 /TiO 2 Nanotube Electrode and Its Photoelectrocatalytic Performance in Dye Wastewater Degradation

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Solar photocatalytic degradation of dye wastewater in the presence of heat‐treated anatase TiO<sub>2</sub>powder

A Photocatalytic Rotating Disc Reactor with Tio2 Nanowire Arrays Deposited for Industrial Wastewater Treatment

Design of Thin Film Photocatalysts Deposited on Rotating Disks for Degradation of Organic Dyes in Wastewater

Enhanced photocatalytic degradation of methylene blue using a novel counter-rotating disc reactor

Photoelectrocatalytic Degradation of Dyes in Aqueous Solution Using CNT/TiO2Electrode

Photocatalytic Degradation of Textile Dyeing Wastewater Using Titanium Dioxide on a Fixed Substrate: Optimization of Process Parameters and Continuous Reactor Tests

Efficient degradation of dye pollutants on nanoporous polyoxotungstate–anatase composite under visible-light irradiation

Efficient Degradation of Phenolic Wastewaters by a Novel Ti/PbO2-Cr-PEDOT Electrode with Enhanced Electrocatalytic Activity and Chemical Stability

Study on the Degradation Process of Photo-Assisted Electro-Catalytic Degradation of Azo Dye Acid Orange Ⅱ

Efficient photoelectrocatalytic degradation of tylosin on TiO2 nanotube arrays with tunable phosphorus dopants

The Promoted Photoelectrocatalytic Degradation of Rhodamine B over Tio2 Thin Film under the Half-Wave Pulsed Direct Current