Compatibility of osteoblasts on four kinds of biomimetic composite scaffolds of bone tissue engineering
Mei-xia Zhang,Chun-rong Yang,Yao Yao,Shao-xiong Min,Miao Li,An-min Jin
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.27.017
2008-01-01
Abstract:Background: In vitro cell culture in the biomimetic physiological condition is a convenient method to prevent the biomaterials from multiple factors in vivo, and to control the experimental conditions with potent reproducibility. Objective: To explore the compatibility of osteoblasts culturing on four kinds of biomimetic composite scaffolds, which are prepared modified bioactive glass (BG), collagen (COL), hyaluronic acid (HYA) and phosphoserine (PS). Design, time and setting: The controlled experiment was conducted in the Clinical Medicine Research Institute of Zhujiang Hospital, Southern Medical University (Guangzhou, Guangdong, China) from March to August in 2006. Materials and methods: Mouse embryo osteoblasts were offered by the Department of Pathogenic Biology in Zhejiang University Medical College. Four kinds of biomimetic three-dimensional composite scaffolds of bone tissue engineering were prepared by means of freeze drying and biomimetic mineralization. Mouse embryo osteoblasts were seeded on the four kinds of composite scaffolds and 58S BG scaffold, respectively. Main outcome measures: At 1, 3 and 5 days of the culture, MTT assay was employed to detect the activity of osteoblasts, alkaline phosphatase activity was assayed with potassium ferricyanide method. Inverted phase contrast microscopy was performed to analyze the dynamic change of osteoblasts. Effects of biomimetic composite scaffolds on cell morphology, growth and proliferation were observed under scanning electron microscope. Results: The osteoblasts activity and alkaline phosphatase activity showed the best outcomes in the BG-COL-HYA-PS, and then BG-COL-PS, BG-COL-HYA, BG-COL, but poor in 58S BG group. There were significant differences among the groups (P < 0.05). The alkaline phosphatase activity was of insignificant differences between BG-COL-HYA-PS scaffold and BG-COL-PS scaffold (P > 0.05). The activities of osteoblasts and alkaline phosphatase were increased as time going on, with the significant differences at each time point (P < 0.05). Osteoblasts adhered well on the BG-COL-HYA-PS scaffolds, but poorly on 58S BG scaffold and even gradually died. Conclusion: The biomimetic BG-COL-HYA-PS composite scaffold has a remarkable promotion on the osteoblasts adhesion, growth, secretion and migration, indicating well compatibility. This composite scaffold has similar biological effects to natural bones and is superior to other three materials.