Abstract:The polysiloxane microspheres varied from 2 μm to 9 μm as light scattering agents were dispersed in acrylate resin to get a coating solution.Then the coating solution was applied to one surface of a polyethylene terephthalate(PET) film having a thickness of 180 μm and dried to form a light scattering film.The influence of the concentration and the particle diameter of the light scattering agents,and the thickness of the coating on the optical property of the scattering film were studied.The application of the polysiloxane microspheres as light scattering agents indicated that the microspheres could significantly(improve) the haze of the scattering film while the film still has good transmittance. When the polysiloxane(microsphere) with the diameter of 5 μm was added to the coating with the thickness of 90 μm,the mass content of 25%,the haze of film is 88%,the transmittance is 90% and the scattering coefficient is 79%.