Strength Theory, A Better Explanation For Top-Down Cracking In Asphalt Pavement

Lu Jia,Lijun Sun,Xiaodi Hu

DOI: https://doi.org/10.1201/9780203882191.ch34

2008-01-01

Abstract:With fast increasing traffic volume and axle load, a common mode of distress, single or parallel longitudinal cracks, often observed at the surface of asphalt pavement. After taking cores on suspect crackings from sites, it was identified that most of those crackings initiated at pavement surface and propagated downward, therefore they were named Top-Down Cracking (TDC). Because TDC often occur on the heavy-duty pavements, the heavy traffic loads were regarded as the main failure reason for TDC. In fact, there were two different prospectives on cause of TDC. One is high surface horizontal tensile stresses due to non-uniform-distributed tire-pavement contact pressure. The other is high shear stress in wearing course also induced by non-uniform-distributed tire-pavement contact pressure. Before the natural characteristics of TDC been completely understood, it has to be concluded in dilemma that both tensile-type cracking and shear-type cracking could initiate TDC. However in strength theory, both the shear failure and tensile failure are sort of simple yield criterions, reflecting the failure of materials in simple stress states, like the materials in the uniaxial tension test and direct shear test. But they are totally different with the stress response in asphalt pavement caused by complex non-uniform-distributed pressure between tire and pavement. In order to explain the real failure reason for TDC, in this paper the measured tire-pavement contact pressure and 31) finite element method (FEM) were used to analyze the mechanical response of asphalt pavement structures. Comparing with the tensile or shear stress failure theories, the TDC is simulated and explained by either Mohr-Coulomb strength theory or Mises strength theory. The analysis results show that the strength theory of complex stress state can better explain the TDC than the traditional theories, such as maximum tensile stress or maximum share stress.