Abstract:Objective: To develop a biodegradable implantable bone material with compatible mechanics with the bone tissue, providing a new biomaterial for clinical bone repair and regeneration. Methods: Silk reinforced polycaprolactone composites (SPC) containing 20%, 40%, and 60% silk were prepared by layer-by-layer assembly and hot-pressing technology. Macroscopic morphology was observed and microstructure were observed by scanning electron microscopy, compressive mechanical properties were detected by compression test, surface wettability was detected by surface contact angle test, degradation of materials was observed after soaking in PBS for 180 days, and proliferation of MC3T3-E1 cells was detected by cell counting kit 8 assay. Six Sprague Dawley rats were subcutaneously implanted with polycaprolactone (PCL) and 20%-SPC, respectively. Masson staining was used to analyze the in vivo degradation behavior and vascularization effect within 180 days. Results: The pore defects of the three SPC sections were relatively few. In the range of 20% to 60%, as the silk content increased and the PCL content decreased, the interlayer spacing of silk fabric decreased, and the fibers almost covered the entire cross-section. The compressive modulus and compressive strength of SPC showed an increasing trend, and the compressive modulus of 60%-SPC was slightly lower than that of 40%-SPC. There were significant differences in compressive modulus and compressive strength between the materials ( P<0.05). In vitro simulated fluid degradation experiments showed that the mass loss of the three types of SPC after 180 days of degradation was within 5%, with the highest mass loss observed in 60%-SPC. The differences in mass loss between the materials were significant ( P<0.05). As the silk content increased, the static water contact angle of each material gradually decreased, and all could promote the proliferation of MC3T3-E1 cells. The subcutaneous degradation experiment in rats showed that 20%-SPC began to degrade at 30 days after implantation, and material degradation and vascularization were significant at 180 days, which was in sharp contrast to PCL. Conclusion: SPC has the mechanical and hydrophilic properties that are compatible with bone tissue. It maintains its mechanical strength for a long time in a simulated body fluid environment in vitro, and achieves dynamic synchronization of material degradation, tissue regeneration, and vascularization through the body's immune regulation mechanism in vivo. It is expected to provide a new type of implant material for clinical bone repair.

Mechanical Strength and in Vitro Degradation of a Silk Scaffold for Tissue-Engineered Ligaments

Silk-Based Scaffold for Ligament Tissue Engineering

From Common Biomass Materials to High-Performance Tissue Engineering Scaffold: Biomimetic Preparation, Properties Characterization, in Vitro and in Vivo Evaluations

In Vitro and In Vivo Degradation, Mechanical Properties, and Histocompatibility of Weft-Knitted Silk Mesh-Like Grafts

The effects of silk layer-by-layer surface modification on the mechanical and structural retention of extracellular matrix scaffolds.

Development of a Silk Cable-Reinforced Gelatin/silk Fibroin Hybrid Scaffold for Ligament Tissue Engineering.

Effect of silk fibroin on degradation and in vivo biocompatibility of poly (L-lactic-co-ε-caprolactone)electronspun nanofibrous scaffolds

An In Vitro Macrophage Response Study of Silk Fibroin and Silk Fibroin/Nano-Hydroxyapatite Scaffolds for Tissue Regeneration Application

In vivo study of anterior cruciate ligament regeneration using mesenchymal stem cells and silk scaffold.

Synergic Combination Of Collagen Matrix With Knitted Silk Scaffold Regenerated Ligament With More Native Microstructure In Rabbit Model

Silk Structure and Degradation.

Ligament regeneration using a knitted silk scaffold combined with collagen matrix

Wet-Spun Silk Fibroin Scaffold with Hierarchical Structure for Ligament Tissue Engineering

Modification of Sericin-Free Silk Fibers for Ligament Tissue Engineering Application

Distinct Tissue Responses to Porous Silk Fibroin Scaffolds (psfss) and Polyvinyl Alcohol (PVA) Sponges in Vivo

[Physical, chemical, and biological property of silk reinforced polycaprolactone composites for bone tissue engineering]

A simple semi-quantitative approach studying the in vivo degradation of regenerated silk fibroin scaffolds with different pore sizes.

A preliminary study on the histocompatibility of silk fibroin

Woven Silk Fabric-Reinforced Silk Nanofibrous Scaffolds for Regenerating Load-Bearing Soft Tissues.

A Nontoxic and Biocompatible Method for Augmenting Mechanical Strength of Acellular Matrix by Silk Fibroin Impregnation

Biomechanical properties of compound ligament with small intestinal submucosa wrapping silk fibers