Abstract:Magnesium hydride has been seen as a potential material for solid state hydrogen storage, but the kinetics and thermodynamics obstacles have hindered its development and application. Three-dimensional flower-like TiO2@C and TiO2 were synthesized as the catalyst for MgH2 system and great catalytic activities are acquired in the hydrogen sorption properties. Experiments also show that the flower-like TiO2@C is superior to flower-like TiO2 in improving the hydrogen storage properties of MgH2. The hydrogen desorption onset and peak temperatures of flower-like TiO2 doped MgH2 is reduced to 199.2 degrees C and 245.4 degrees C, while the primitive MgH2 starts to release hydrogen at 294.6 degrees C and the rapid dehydrogenation temperature is even as high as 362.6 degrees C. The onset and peak temperatures of flower-like TiO2@C doped MgH2 are further reduced to 180.3 degrees C and 233.0 degrees C. The flower-like TiO2 @C doped MgH2 composite can release 6.0 wt% hydrogen at 250 degrees C within 7 min, and 4.86 wt% hydrogen at 225 degrees C within 60 min, while flower-like TiO2 doped MgH2 can release 6.0 wt% hydrogen at 250 degrees C within 8 min, and 3.89 wt% hydrogen at 225 degrees C within 60 min. Hydrogen absorption kinetics is also improved dramatically. Moreover, compared with primitive MgH2 and the flower-like TiO2 doped MgH2, the activation energy of flower-like TiO2@C doped MgH2 is significantly decreased to 67.10 kJ/mol. All the improvement of hydrogen sorption properties can be ascribed to the flower-like structure and the two-phase coexistence of TiO2 and amorphous carbon. Such phase composition and unique structure are proved to be the critical factor to improve the hydrogen sorption properties of MgH2, which can be considered as the new prospect for improving the kinetics of light-metal hydrogen storage materials. (C) 2019 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. and Science Press. All rights reserved.

Preparation and Characterization of Mg/TiO2 Nanocomposite Particles by Hydrogen Plasma-Metal Reaction

Highly Dispersed Metal Nanoparticles on TiO2 Acted As Nano Redox Reactor and Its Synergistic Catalysis on the Hydrogen Storage Properties of Magnesium Hydride

Excellent Synergistic Catalytic Mechanism of In-Situ Formed Nanosized Mg2Ni and Multiple Valence Titanium for Improved Hydrogen Desorption Properties of Magnesium Hydride

Preparations and Characteristics of Ti Hydride and Mg Ultrafine Particles by Hydrogen Plasma–metal Reaction

Investigation of catalytic modification of light magnesium based hydrogen storage material

EFFECT OF TiO2 NANOPARTICLES ON THE HYDRIDING AND DEHYDRIDING PROPERTIES OF Mg-15wt%Mg2Ni COMPOSITES

Excellent catalysis of TiO2 nanosheets with high-surface-energy {001} facets on the hydrogen storage properties of MgH2.

Superior hydrogen storage kinetics of MgH2 nanoparticles doped with TiF3

Synthesis of Fe-Al Nanoparticles by Hydrogen Plasma-Metal Reaction

Preparation of Mg-based hydrogen storage materials from metal nanoparticles

Superior De/hydrogenation Performances of MgH2 Catalyzed by 3D Flower-Like TiO2@C Nanostructures

Hydrogen Storage Properties of Mg+10% TiFe_(1-x)Cr_x(x=0,0.3) Multi-Phase Alloys

Preparation and hydrogen storage properties of Mg-20 wt.% Mg 2Ni0.8Cr0.2 composite with TiO2 nanoparticles

Phase-structure and Hydrogen Storage Behaviors of Mg+10％ Ni2P Composite Prepared by Reactive Ball-Milling

Synthesis of magnesium nanoparticles with superior hydrogen storage properties by acetylene plasma metal reaction

Preparation of Mg2Ni Intermetallic Compound from Nanoparticles

Achieving superior hydrogen storage properties of MgH<sub>2</sub> by the effect of TiFe and carbon nanotubes

Enhanced hydrogen storage properties of magnesium by the synergic catalytic effect of TiH 1.971 and TiH 1.5 nanoparticles at room temperature

Improved hydrogen storage properties of Mg-V nanoparticles prepared by hydrogen plasma-metal reaction

Preparation and Hydrogen Sorption Properties of a Ni Decorated Mg Based Mg@Ni Nano-Composite

Achieving Superior Hydrogen Sorption Kinetics of MgH2 by Addition of Ni-doped TiO2 Catalysts