Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Preparation of Nitrogen-Doped Triple-Walled Carbon Nanotubes

Controllable preparation of triple-walled carbon nanotubes and their growth mechanism.

Investigation of the Fabrication and Structure of Double-Wall Carbon Nanotubes

Preparation of highly pure double-walled carbon nanotubes

Nitrogen-doped carbon nanotubes synthesized with carbon nanotubes as catalyst

Preparation of highly oxidized nitrogen-doped carbon nanotubes

Preparation of Double-Walled Carbon Nanotubes

Growth of carbon nanotubes and nitrogen-doped carbon nanotubes on “carbon nanotube seeds”

Structural and Compositional Regulation of Nitrogen-Doped Carbon Nanotubes with Nitrogen-Containing Aromatic Precursors

Controllable preparation and properties of single-/double-walled carbon nanotubes

Filling Double-Walled Carbon Nanotubes with WO3 and W Nanowires Via Confined Chemical Reactions.

Synthesis, Photoluminescence, and Magnetic Properties of Nitrogen-Doping Helical Carbon Nanotubes

Preparation and Subsequent Characterization of Sulfur and Nitrogen Dual-doped Carbon Nanotubes

Doped Carbon Nanotube Array with a Gradient of Nitrogen Concentration

High-pressure pyrolysis of melamine route to nitrogen-doped conical hollow and bamboo-like carbon nanotubes

Synthesis and Enhanced Field-Emission of Thin-Walled, Open-Ended, and Well-Aligned N-Doped Carbon Nanotubes

Nitrogen‐Doped Single‐Walled Carbon Nanotubes Grown on Substrates: Evidence for Framework Doping and Their Enhanced Properties

Scanning Transmission X-ray Microscopy and X-ray Absorption Near-Edge Structure Studies of N-doped Carbon Nanotubes Sealed with N2 Gas

Raman and XPS analyses of pristine and annealed N-doped double-walled carbon nanotubes

Atomic configuration of nitrogen-doped single-walled carbon nanotubes

Structural and electronic properties of double-walled G-C3N4 nanotubes: a density functional theory study