Crystal Growth Mechanism Changes in Pseudo-Dewetted Poly(Ethylene Oxide) Thin Layers
Dun-Shen Zhu,Yi-Xin Liu,Er-Qiang Chen,Ming Li,Chao Chen,You-Hai Sun,An-Chang Shi,Ryan M. Van Horn,Stephen Z. D. Cheng
DOI: https://doi.org/10.1021/ma062542s
IF: 5.5
2007-01-01
Macromolecules
Abstract:Changes in the crystal growth mechanism were observed in pseudo-dewetted, thin layers of low molecular weight (MW) poly(ethylene oxide) (PEO) on a hydrophilic mica surface. The studies were conducted using two PEO fractions (HPEO and MHPEO) with similar MW's (number-average MW of around 4500 g/mol) but different end-group chemistries. For the HPEO, both ends of the chain are capped by -OH groups. For the MHPEO, one end is capped by an -OH group, while the other end is capped by an -OCH3 group. Utilizing in-situ atomic force microscopy, the growth of single crystals as a function of time (t) was monitored at different crystallization temperatures (T-x). Depending on the end-group chemistry and T-x applied, two growth laws were observed, which state that the crystal lateral size r or the crystal volume V can be linearly proportional to t (r proportional to t or V proportional to t). Combined with morphological observations of the single crystals, it could be deduced that when r proportional to t, the crystal growth was nucleation-limited (NL), while in the case of V proportional to t, and thus r proportional to t(0.5) at constant crystal thickness, the crystal growth was diffusion-limited (DL). A change of the crystal growth mechanism from the NL to the DL process was also observed with decreasing T-x in the MHPEO sample.