Characterization and Tribological Investigation of Self-assembled 3-Mercaptopropyl Trimethoxysilane Deposited on Glass Substrates

BAI Tao,CHENG Xian-hua

DOI: https://doi.org/10.3321/j.issn:1006-2467.2007.02.027

2007-01-01

Abstract:Self-assembled monolayer was fabricated on hydroxylated glass substrates by molecular self-assembly process.Atomic force microscope(AFM) and Xray photoelectron spectrometry(XPS) were used to characterize the thin films.Water contact angle measurements indicate that the ratio of MPTS absorbed on silicon substrate increases with increasing time.The chemical states of some typical elements in the MPTS-SAM were analyzed using X-ray photoelectron spectroscopy. The morphology of the MPTS-SAM was observed using an atomic force microscope.The tribological properties of the as-prepared thin films sliding against a steel ball were evaluated on a friction and wear tester.The results show that the MPTS-SAM is prepared on the glass slide at a film-formation duration of 90min,the corresponding MPTS-SAM shows almost no change in the water contact angle,which indicates that the self-assembly process of the MPTS monolayer is completed in 90min.Moreover,the MPTS-SAM has good friction-reducing and antiwear ability as it slides against the steel counterpart at a small load.The tribological experiment shows that the friction coefficient of glass substrate reduces from 0.85 to 0.19 after the formation of MPTSSAM on its surface.