PREPARATION AND MICROSTRUCTURE OF KAOLINITE-ACETAMIDE INTERCALATION COMPOUNDS

ZHANG Sheng-hui,WANG Zhen-zhong,SHEN Cheng-jin,XIA Hua

DOI: https://doi.org/10.3969/j.issn.1001-6872.2007.02.002

2007-01-01

Abstract:Acetamide was intercalated into kaolinite directly by melting intercalation method.The pure kaolinite-acetamide intercalation compounds are obtained by washing products with ethanol in the absence of water.The basal spacing of kaolinite-acetamide intercalation compounds increased to 1.102 nm from 0.721 nm.Intercalation caused red shifts of the inner surface OH stretching bands from 3 651 cm-1 to 3 647 cm-1 in the kaolinite-acetamide intercalation compounds and deforming bands from 911 cm-1 to 907 cm-1,and the NH vibrations at 3 211 cm-1 and 3 390 cm-1 disappeared with a new band appearing at 3 478 cm-1.These IR band changes implied the breaking of the H-bonds between layers of kaolinite and the formation of new H-bonds between the inner-surface hydroxyls of the kaolinite and the amino groups of acetamide in the intercalation compounds.The shifts of both the inner OH stretching bands from 3 616 cm-1 to 3 611 cm-1 and the Si—O bands of kaolinite showed acetamide CH group was partly keyed into the ditrigonal hole.A model was provided to analyse the microstructure of kaolinite-acetamide intercalation compounds.The results show that computation data is in good agreement with experimental data.