Abstract:Ethanol oxidation reaction (EOR) is a common anode process for direct ethanol fuel cell (DEFC) and ethanol reforming electrolyzer. Au@Pt and AuPt alloy are widely used bimetallic catalysts, yet no comparative study has been reported of electrocatalysis of EOR on these two differently structured catalysts. The present work aims to synthesize and characterize carbon supported Au@Pt and AuPt with controlled composition and size, and compare their electrocatalytic activities and stabilities toward EOR in alkaline media. For the synthesis of Au@Pt/C, a 5-nm Au colloid was first obtained by adding excessive amount of sodium borohydride to a chloroauric acid precursor containing sodium citrate with a mixed ice-water bath. CO gas was bubbled into the Au colloidal solution at 60 degrees C under strong stirring to reduce a desired amount of potassium tetrachloroplatinate(II) to terminate Pt quasi-monolayer shell on Au nanoparticle core. A sonicated carbon black (Vulcan XC-72) aqueous slurry was then dropwise added to the above Au@Pt colloid, and the mixture was kept stifling for 48 h to ensure the exhaustive loading of Au@,Pt nanoparticles onto the carbon support. For the synthesis of AuPt/C with the same Au:Pt molar ratio and metal loading as that for Au@Pt/C, coreduction of the Au(III) and Pt(II) species was attained by using sodium borohydride as the reducing agent with the rest procedures being same as the above mentioned. X-ray diffractometry (XRD) revealed that the diffraction peaks for Au@Pt/C were virtually same as those for Au/C, consistent with a Pt quasi-monolayer, while the diffraction peaks for AuPt/C located in between those for Au/C and Pt/C. X-ray photoelectron spectroscopy (XPS) results were consitent with the different structures of the two catalysts, and the Pt core level shift suggested an upshift of Pt d-band center for both bimetallic catalysts. Cyclic voltammetry and chronoamperometry revealed markedly increased EOR current on Au@Pt/C and AuPt/C, as compared to that of Pt/C and Au/C. CO-stripping voltammetry on Au@Pt/C and AuPt/C indicated that surface reconstruction occurred by potential cycling, resulting in a decrease of ex- posed Pt sites but not the electrocatalytic activities. H-1 NMR analysis confirmed the C2 pathway is predominant. Nevertheless, Au@Pt/C outperformed AuPt/C and Pt/C with a lower onset oxidation potential and a higher peak current for EOR, as well as a slightly higher selectivity toward C1 pathway. Although the synergetic effect of Au-Pt bimetallic interface for EOR is not well understood, the enhanced adsorption of ethanol, OH, acetyl and CO on Pt sites may be accountable for the observed results.

Electrochemical Characterization of Pt-CeO2/C and Pt-CexZr1−xO2/C Catalysts for Ethanol Electro-Oxidation

Promoting Effect of CeO2 in the Electrocatalytic Activity of Rhodium for Ethanol Electro-Oxidation

CO and Methane Oxidation Over CeXZr1-XO2 Mixed Oxide Supported PdO Catalysts

Effect of Ce/Zr Atomic Ratio on the TWC Properties of PdO/CexZr1-xO2(x=0-1.0) Catalysts

Cataluminescence and Catalytic Reactions of Ethanol Oxidation over Nanosized Ce1−xZrxO2 (0 ⩽ X ⩽ 1) Catalysts

Electrochemical oxidation of ethanol on Pt–ZrO2/C catalyst

Catalytic oxidation cataluminescence of ethanol over catalysts

Electro-oxidation of Ethanol on Pt-ZrO_2/C Electrocatalyst in Alkaline Media

Low temperature catalytic combustion of ethanol over Pt/γ-Al2O3/CexZr1-xO2 honeycomb catalysts

Structural designing of Pt-CeO2/CNTs for methanol electro-oxidation

Comparative study of Pt/CeO2-CNTs and PtRu/C as methanol electro-oxidation catalysts

Complete Oxidation of Ethanol and Thermal Stability of Ceria-BasedMaterials Modified by Doping Cu

Catalytic Combustion of VOCs on Pt/CuMnCe and Pt/CeY Honeycomb Monolithic Catalysts

Propene and CO Oxidation on Pt/Ce-Zr-SO 4 2– Diesel Oxidation Catalysts: Effect of Sulfate on Activity and Stability

Enhanced catalytic oxidation of diluted ethylene oxide on Pt/CeO<sub>2</sub> catalyst under low temperature

Discuss on Mechanism of CO Electro-Oxidation with Pt-ZrO2/C Catalyst

Effect of Ceria on Carbon Supported Platinum Catalysts for Methanol Electrooxidation

The Effect of Ceo2 on Pt/Ceo2/Cnt Catalyst for Co Electrooxidation

Controlled Synthesis of Gold-Platinum Catalysts for Ethanol Electro-oxidation Reaction

Integrated Catalyst ZnNC⊂PtZn for High‐performance Ethanol Electrooxidation and DEFC

Pt/C and Pt/SnOx/C Catalysts for Ethanol Electrooxidation: Rotating Disk Electrode Study