Abstract:Zn-exchanged ZSM-5-Al2O3 (ZA) composite-supported Pt/NiMo (NM) sulfided catalysts were prepared using the conventional kneading method and were tested for dehydrocyclization-cracking of soybean oil. The effects of Zn addition on the activity and selectivity of products were investigated under moderate-pressure conditions of 0.5 and 1.0 MPa H2 in the temperature range of 420-580 °C. At the temperature 500 °C and higher, most of the sample soybean oil was converted at both the pressures of 0.5 and 1.0 MPa. At 1.0 MPa and 500 °C, the effects of Zn addition appeared and increased the yields of aromatics, while the catalyst without Zn produced larger amounts of products with more than C18. Further, at 0.5 MPa and 580 °C, the gas formation was inhibited in comparison to the cases of 1.0 MPa and the effects of the Zn addition also appeared and increased the yields of aromatics, while the catalyst without Zn produced larger amounts of products with more than C18. The Pt/NM/Zn(122)ZA test catalyst produced more than 63% of liquid fuels in the range C5-C18, and the yield of aromatics was 13%, the maximum value in the present study. The following reaction routes were proposed. The structure of triglyceride is converted by hydrocracking to three molecules of aliphatic acids and propane on the surface PtNiMo sulfide on Al2O3 support. The converted aliphatic acids are decomposed through decarboxylation to hydrocarbon fragments, which are further decomposed by cracking on the acid sites of the catalyst, the surface of NiMo sulfide, Al2O3, or ZSM-5. Finally, the formed C3 and C4 olefins are transformed to aromatics through the Diels-Alder reaction on the Zn species of ZnZSM-5. On the other hand, although gases were relatively small in amount, aromatic compounds were formed significantly, suggesting that cyclization might directly occur without conversion to gaseous hydrocarbons to some extent.

Catalytic Performance of ZSM-5 Catalyst Modified by Sodium Hydroxidefor C_4-Olefin Cracking

Catalytic Cracking Reactions Of C-4-Olefin Over Zeolites H-Zsm-5, H-Mordenite And H-Sapo-34

Synthesis of ZSM-48 zeolites and their catalytic performance in C4-olefin cracking reactions

ZSM-5 Catalysts Modified with Lanthanum for Catalytic Cracking of C4-olefins to Propylene

Effects of post treatment of HZSM-5 zeolites on catalytic cracking of butene

Characterization and Catalytic Performance of (Nh4)2sif6-Modified HZSM-5 Catalyst for C4 Olefin Cracking

The Adsorption and Catalytic Cracking of C8 Hydrocarbons on HZSM-5 Zeolite

ZSM–5@KIT–6 encapsulated composite molecular sieves for the catalytic cracking of waste cooking oil model compound to produce light olefins

Preparation of nano ZSM-5 with hydrophobic surfaces and application to catalytic cracking of hydrocarbon fuels

Catalytic oxidation of isoamyl alcohol on modified ZSM-5 molecular sieve catalysts prepared by different methods

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

Hierarchical ZSM-5 zeolite designed by combining desilication and dealumination with related study of n-heptane cracking performance

Effects of the controllable mesostructure of nano-sized ZSM-5 on the co-cracking of phenolic bio-oil model compounds and ethanol

Synthesis of Nanoscale ZSM-5 Zeolites for the Catalytic Cracking of Oleic Acid into Light Olefins and Aromatics

Effects of Zn Addition into ZSM-5 Zeolite on Dehydrocyclization-Cracking of Soybean Oil Using Hierarchical Zeolite-Al2O3 Composite-Supported Pt/NiMo Sulfided Catalysts

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of n-Decane

Strategies To Enhance The Catalytic Performance Of Zsm-5 Zeolite In Hydrocarbon Cracking: A Review

Optimization and modification of ZSM-5 zeolite for efficient catalytic cracking of 1,2-dichloroethane

Effect of Si/Al ratio on performance of Pt–Sn-based catalyst supported on ZSM-5 zeolite for n-butane conversion to light olefins

Process for catalytic cracking naphtha coupled with methanol using modified zsm 5 molecular sieve catalyst

Effect of phosphorus on HZSM-5 catalyst for C4-olefin cracking reactions to produce propylene