Broadband near-infrared emission covering S+C+L in Er3+-doped nanocrystal modified PbO-PbF2-Bi2O3-Ga2O3 glasses
Jin Yu,Kang Li,Xiaotong Zhao,Shunbin Wang,Gerald Farrell,Shijie Jia,Pengfei Wang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.09.027
IF: 5.7
2023-09-01
Journal of the European Ceramic Society
Abstract:This paper reports a broadband near-infrared emission ranging from 1400 to 1660 nm in Er3+-doped nanocrystal-modified PbO-PbF2-Bi2O3-Ga2O3 glasses. After heat treatment, X-ray diffraction measurements were performed and confirmed that PbBiO2F nanocrystals were precipitated in the precursor glasses. As nanocrystals alter the local environment around Er3+ ions, the emission spectrum of the transition 4I13/2→4I15/2 is broadened and enhanced, resulting in a broadband emission and an FWHM wavelength range of 143.4nm from 1470.1 to 1613.5nm, which overlaps the S+C+L optical communications windows. In addition, the emission intensity of the 4I11/2→4I13/2 transition is also found to be increased after heat treatment, thus enhancing the λ~2750nm emission intensity. Our results indicate that an Er3+-doped nanocrystal-modified PbO-PbF2-Bi2O3-Ga2O3 glass could be a competitive candidate material that can offer improved bandwidths for S+C+L broadband amplifiers used in very high-capacity optical communications systems.
materials science, ceramics