Photoinduced birefringence and relaxation of film in a highly stable azobenzene containing copolymer
ZhangYuan Lei,Jintang Huang,Wu Si,Zhang Qijin,Keyi Wang
DOI: https://doi.org/10.3969/j.issn.1007-2276.2011.08.022
2011-01-01
Infrared and Laser Engineering
Abstract:A new azobenzene containing copolymer,which is polymerized by 4-((4-hydroxyphenyl)diazenyl) benzonitrile and poly(6-(4-(pyridin-4-yldiazenyl)phenoxy)hexyl methacrylate),was synthesized in this paper.A linearly polarized light inducing device was set up and the photoinduced birefringence and relaxation curve of the azobenzene containing copolymer with different molar ratio(0,0.25,0.5,0.75,1) were measured.Aging test and repeated writing and erasing test were carried out.Experimental results show this copolymer is very stable,the larger the molar ratio,the higher the photoinduced birefringence.It is a notable case when the molar ratio is less than fifty percent,the relaxation curve declines firstly and then keeps changeless basically.But when the molar ratio is larger than fifty percent,the relaxation curve rises firstly and then keeps changeless basically.It comes to the conclusion that the sample with the molar ratio lager than fifty percent is more stable and has higher capability of saving written information.