Abstract:The effect of interface roughness of ferromagnetic and antiferromagnetic layers on exchange bias is still not well understood. In this report we have investigated the effect of surface roughness in (111)-oriented antiferromagnetic CoO films on exchange bias with ferromagnetic Fe grown on top. The surface roughness is controlled at the atomic scale, over a range below similar to 0.35 nm, by varying layer thickness of the CoO films. It is observed that both exchange-bias field (H-E) and coercivity (H-C) extensively depend on the atomic scale roughness of the CoO (111) at the interface with Fe film. An opposite dependence of H-E and H-C on interface roughness was found, which was ascribed to partially compensated spin states induced by the atomic roughness at the fully uncompensated CoO (111) surfaces and was corroborated using Monte Carlo simulations. Moreover, the onset temperature for H-C is found to be up to similar to 80 K below the blocking temperature (T-B) and the temperature dependence of H-C follows the power law with a critical exponent equal to one, which indicates that, in this system, H-C is more of an interface-related property than H-E.

Theoretical Investigation of Exchange Bias

Theoretical Investigation of Exchange Bias in Compensated Cases

Quantum Statistical Calculation of Exchange Bias

EXCHANGE BIAS IN FERROMAGNETIC/ANTIFERROMAGNETIC BILAYERS

The Exchange Bias and Coercivity of FM/AFM Films: Monte Carlo Simulation

Exchange Bias in Ferromagnetic/compensated Antiferromagnetic Bilayers

Exchange Bias in (110)-Orientated Bi0.9la0.1feo3/La0.5ca0.5mno3 Films

Thickness and angular dependencies of exchange bias in ferromagnetic/antiferromagnetic bilayers

Micromagnetic approach to exchange bias---A new look at an old problem

Exchange Bias with Interacting Random Anti-ferromagnetic Grains

Exchange bias in (1 1 0)-orientated Bi 0.9La 0.1FeO 3/La 0.5Ca 0.5MnO 3 films

Angular Dependence of Positive Exchange Biasing in GdFe∕FeMn Bilayers

Ferromagnetic Resonance and Exchange Anisotropy in Ferromagnetic/antiferromagnetic Bilayers

Measurement of Exchange Anisotropy in Exchange-Bias Bilayers

Anomalous Exchange Bias in Gd/Cr Bilayer and Cr/Gd/Cr Trilayers

Domain State Model for Exchange Bias

Hysteretic Behavior of Angular Dependence of Exchange Bias in FeNi/FeMn Bilayers

Influence of Atomic Roughness at the Uncompensated Fe/CoO(111) Interface on the Exchange-Bias Effect

The Effect of Interfacial Coupling in Co/CoO Exchange-Bias Bilayers with Special Field Cooling

Local breaking of the spin-orbit interaction: the microscopic origin of exchange bias in Co/FeMn

Stacking-dependent exchange bias in two-dimensional ferromagnetic/antiferromagnetic bilayers