Abstract:The size dependence of ductile to brittle transition of Zr-based metallic glasses was systematically investigated by small punch test. It was found that the metallic glasses with thickness ranging from 50 to 700 μm displayed an obvious transition from ductility to brittleness. Compared with thick samples, thin samples exhibit higher strength and better plasticity, which is attributed to the size-dependent transformation from soft state to hard state dominated by the deformation factor (<math>α=τ/σ</math>). Specifically, two significant transitions in deformation behavior at sample thickness of 200 and 500 μm are attributed to two critical deformation factors of <math>αc1</math> and <math>αc2</math>, which are responsible for the initiation of circumferential and radial shear bands, respectively. Specifically, only several micro-cracks can be observed on sample surface with <math>α≤αc2</math>. While <math>αc1≥α≥αc2</math>, multiple radial shear bands are activated and uniformly distributed on the sample surface. Further, when <math>α≥αc1</math>, multiple circumferential shear bands primarily initiate under high shear stress and large number of radial and circumferential shear bands can be observed on sample surface. The initiation and interaction of multiple radial and circumferential shear bands significantly enhance the ductility of the samples with <math>α≥αc1</math>.

Multiplication of Shear Bands and Ductility of Metallic Glass

The Shear Band Controlled Deformation in Metallic Glass: A Perspective from Fracture

Tensile ductility and necking of metallic glass

Enhancing tensile ductility of porous metallic glasses through shear band path design

The Multiple Shear Bands and Plasticity in Metallic Glasses: A Possible Origin from Stress Redistribution

Initiation and Evolution of Shear Bands in Bulk Metallic Glass under Tension—an in Situ Scanning Electron Microscopy Observation

Effect of Pre-Existing Shear Bands on the Tensile Mechanical Properties of A Bulk Metallic Glass

Intrinsic tensile ductility in strain hardening multiprincipal element metallic glass

"Ductile" Fracture of Metallic Glass Nanolaminates

Uniform Tensile Elongation in Framed Submicron Metallic Glass Specimen in the Limit of Suppressed Shear Banding

A new constitutive model for shear banding instability in metallic glass

Two-Zone Heterogeneous Structure Within Shear Bands of A Bulk Metallic Glass

Shear Band Control for Improved Strength-Ductility Synergy in Metallic Glasses

Deformation Behavior of Metallic Glasses with Shear Band Like Atomic Structure: a Molecular Dynamics Study.

Structural transformation and rheological processes in bulk metallic glass Zr41Ti14Cu12.5Ni10Be22.5

Non-localized deformation in metallic alloys with amorphous structure

Superductile Bulk Metallic Glass

Nonaffine Strains Control Ductility of Metallic Glasses

Size dependence of ductile to brittle transition of Zr-based metallic glasses under multiaxial loading

Formation and dilatation of shear bands in a Cu-Zr metallic glass: A free volume perspective

Densification and heterogeneity enhancement of Fe-based metallic glass under local plastic flow