Abstract:Tensile, compressive, cyclic tension-tension, and cyclic compression-compression tests at room temperature were systematically applied to a Zr52.5Cu17.9Al10Ni14.6Ti5 bulk metallic glass for comprehensive understanding of its damage and fracture mechanisms. Under tensile loading, the metallic glass only displays elastic deformation followed by brittle shear fracture. Under compressive loading, after elastic deformation, obvious plasticity (0.5 to 0.8 pct) can be observed before the final shear fracture. The fracture strength under compression is slightly higher than that under tension. The shear fracture under compression and tension does not occur along the maximum shear stress plane. This indicates that the fracture behavior of the metallic glass does not follow the Tresca criterion. The fracture surfaces show remarkably different features, i.e., a uniform vein structure (compressive fracture) and round cores coexisting with the radiating veins (tensile fracture). Under cyclic tension-tension loading, fatigue cracks are first initiated along localized shear bands on the specimen surface, then propagated along a plane basically perpendicular to the stress axis. A surface damage layer exists under cyclic compression-compression loading. However, the final failure also exhibits a pure shear fracture feature as under uniaxial compression. The cyclic compression-compression fatigue life of the metallic glass is about a factor of 10 higher than the cyclic tension-tension fatigue life at the same stress ratio. Based on these results, the damage and fracture mechanisms of the metallic glass induced by uniaxial and cyclic loading are elucidated.

Tensile Behavior of Bulk Metallic Glasses by in Situ X-Ray Diffraction

Local Strain Behavior of Bulk Metallic Glasses under Tension Studied by in Situ X-Ray Diffraction

Structural transformation and rheological processes in bulk metallic glass Zr41Ti14Cu12.5Ni10Be22.5

Mapping the Strain Distributions in Deformed Bulk Metallic Glasses Using Hard X-Ray Diffraction

Structural Evolution in Bulk Metallic Glass under High-Temperature Tension

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Tensile Elastic Behavior of A Zr-Cu-Ag-Al Bulk Metallic Glass

The Ductile to Brittle Transition Behavior in a Zr-based Bulk Metallic Glass

Tensile fracture morphologies of bulk metallic glass

Tensile Deformation Behaviour of Zr-based Glassy Alloys

Temperature-Induced Ductile-To-Brittle Transition of Bulk Metallic Glasses

Fatigue and fracture behavior of bulk metallic glass

Atomic-Level Structural Modifications Induced by Severe Plastic Shear Deformation in Bulk Metallic Glasses

Investigation of Deformation Behavior of Zr-Ti-Ni-Cu-Be Bulk Metallic Glass Containing Nanocrystals

Tension-Tension Fatigue Behavior of High-Toughness Zr61Ti2Cu25Al12 Bulk Metallic Glass

Criteria for tensile plasticity in Cu–Zr–Al bulk metallic glasses

Ductile to brittle transition of fracture of a Zr-based bulk metallic glass: Strain rate effect

Initiation and Evolution of Shear Bands in Bulk Metallic Glass under Tension—an in Situ Scanning Electron Microscopy Observation

Effect of Pre-Existing Shear Bands on the Tensile Mechanical Properties of A Bulk Metallic Glass

Bulk Metallic Glasses with Large Plasticity: Composition Design from the Structural Perspective

Compressive Fracture Characteristics of A Zr-Based Bulk Metallic Glass at High Test Temperatures