Abstract:Owing to the excellent biocompatibility and corrosion-resistance of titanium and bioactivity of hydroxyapatite, the titanium/hydroxyapatite composite material combining their advantages is a highlight with bright prospects in medical clinics. In the present paper, the microarc oxidation (MAO) was performed on commercial pure titanium at first. Furthermore, the hydrothermal treatment (HT)was given with media of deionized water at 200°C for 4h in an autoclave. The surface morphology of the samples was observed by scanning electron microscopy (SEM), and the detailed composition was analyzed with Energy-Dispersive X-Ray Spectroscopy (EDS). The X-ray diffraction analysis (XRD) was employed to characterize the crystal structure of composite. The results indicate that the titania film contains the Ca and P elements on titanium substrate after MAO, which converts into the hydroxyapatite crystals via hydrothermal treatment. The smaller size and amount of hydroxyapatite crystals are found when lower voltage is presented. But there are converse phenomena with higher voltage, especially, the differences can be neglected above 400V. It is shown that the micro-hole and hollow surface of titania film can induce the hydroxyapatite nucleation and growth as two different forming ways. The hydroxyapatite has a preference of forming in hollow surface with lower voltage, however, the presences of the micro-hole and hollow surface of titania film are occurring for higher voltage. The hydroxyapatite forming in micro-hole shows needle-like crystal and high bonding strength with surrounding titania film because of the mechanical restrict force from micro-hole wall. Also it is noted that hydroxyapatite crystals incline to precipitate on the film surface with high Ca and P concentrations after the hydrothermal treatment.

Structure and in Vitro Bioactivity of Si Enriched Hydroxyapatite/TiO2 Coatings on Pure Titanium by Micro-Arc Oxidation

The structure and in vitro apatite formation ability of porous titanium covered bioactive microarc oxidized TiO2-based coatings containing Si, Na and Ca

Synthesis and Properties of Hydroxyapatite-Containing Porous Titania Coating on Ultrafine-Grained Titanium by Micro-Arc Oxidation

Microstructure and Bioactivity of Ca, P and Sr Doped Tio2 Coating Formed on Porous Titanium by Micro-Arc Oxidation

Effect of Ti-OH Groups on Microstructure and Bioactivity of TiO2 Coating Prepared by Micro-Arc Oxidation

Study on Strontium Doped Bioactive Coatings on Titanium Alloys Surfaces by Micro-Arc Oxidation

Bioactivity Study of the Titanium Plates Treated with Microarc Oxidation and Alkali

Surface Modification of Pure Titanium by Hydroxyapatite-Containing Composite Coatings

Characterization and Cytocompatibility of Hierarchical Porous TiO2 Coatings Incorporated with Calcium and Strontium by One-Step Micro-Arc Oxidation.

Influence of Hydrothermal Treatment in Deionized Water on Surface Morphology and Structure of Titanium with Biomedical Application by Microarc Oxidation

[Preparation of Hydroxyapatite-Containing Titania Film on the Surface of Pure Titanium by Micro-Arc Oxidation Technique].

Characterization of Bioactive Ceramic Coatings Prepared on Titanium Implants by Micro-Arc Oxidation

Surface Microstructure and Cell Biocompatibility of Silicon-Substituted Hydroxyapatite Coating on Titanium Substrate Prepared by a Biomimetic Process

Characteristic and in vitro bioactivity of a microarc-oxidized TiO2-based coating after chemical treatment

Study on Porous Titanium Biomedical Materials

Hydroxyapatite coatings produced on commercially pure titanium by micro-arc oxidation.

Preparation and Characterization of TiO2/silicate Hierarchical Coating on Titanium Surface for Biomedical Applications.

Preparation and Properties of Hydroxyapatite-Containing Titania Coating by Micro-Arc Oxidation

Studies on the Bioceramic Coating on Titamium Substrate Including Silicon and Calcium by Micro-Arc Oxidation and Osteoblast’s Adhesion and Proliferation on the Coating

Bioactive coating with hierarchical double porous structure on titanium surface formed by two-step microarc oxidation treatment

Preparation of Bioactive Hydroxyapatite on Pure Titanium