Abstract:Ni/Al-Al2O3 gradient ceramic coating was prepared on Q235 steel by plasma spraying. Microstructure and corrosion behavior in boiling 5%HCl solution of the samples sprayed with this coating were investigated. The results showed that thickness of Al2O3 ceramic coating was increased greatly and almost no connected pores formed in the gradient coating due to the existent of Ni/Al-Al2O3 transition interlayer coatings. The corrosion resistance of Q235 steel with Ni/Al-Al2O3 gradient composite ceramic coating in boiling 5%HCl solution was greatly improved.

Microstructure and Corrosion Behavior of Ni/Al-Al2o3 Gradient Ceramic Coatings on Q235 Steel