Abstract:A fluorine doped TiO2 Sol (F-TiO2) was prepared by a modified precipitation-sol-hydrothermal crystallization method using TiCl4 as precursor. The influence of F doping, hydrothermal treating temperature and time, pH values of medium on the morphology and crystallization was studied. The structure of as-prepared F-TiO2 Sol was characterized by XRD, UV-Vis-DRS, TEM, TG-DTA, FTIR, XPS, and adsorption capacity determination and surface acidity determination. It was confirmed by XRD that F-TiO2 Sol particles had anatase crystalline structure; moreover, the addition of fluorine could decrease the temperature and shorten the time of process of hydrothermal crystallization, and improve the crystallization of particle significantly. The TEM images indicated that F-TiO2 particles in Sol were spherical, and the average particle size was ca. 6.5 nm. The XPS results showed that fluorine atoms were adopted by TiO2 Sol particles with two forms. One was physically adsorbed on the surface of TiO2, and the other was embedded into TiO2 crystal lattice. The experiments of the determination on interfacial adsorption capacity, surface acidity and the photocatalytic activity found that F-TiO2 Sol had stronger surface acidity, higher adsorption capability and good photocatalytic activity for decomposition of rhodamine B than pure TiO2 Sol and P25 TiO2. Furthermore, the promotion mechanism of fluorine on the photocatalytic activities and structure of TiO2 was discussed based on the separation efficiency theory of charge carrier.

Preparation of anatase F doped TiO 2 sol and its performance for photodegradation of formaldehyde

Preparation and characterization of anatase N–F-codoped TiO2 sol and its photocatalytic degradation for formaldehyde

Preparation, characterization and photocatalytic performance of anatase F doped TiO2 sol

Preparation and characterization of anataseF-TiO2 sol photocatalysts

Preparation and Formaldehyde-Degrading Performance of Photocatalytic Fluorescent Lamp

Preparation of Anatase F-TiO2 and Its Performance for the Photodegradation of 4-Chlorophenol

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

Hydrothermal preparation and photocatalytic performance of fluorine doped titanium dioxide

The Preparation and Characterization of N-F-Sm-TiO2 Sol and Its Photocatalytic Degradation for 4-Chlorophenol

Low-temperature Preparation of F-doped TiO2 Film and Its Photocatalytic Activity under Solar Light

Formaldehyde degradation of waterborne paints over S- and C-doped titanium dioxide under visible light

Preparation of Fe-doped Mixed Crystal TiO2 Catalyst and Investigation of Its Sonocatalytic Activity During Degradation of Azo Fuchsine under Ultrasonic Irradiation.

Photocatalytic Oxidation of Gaseous Formaldehyde on TiO 2 : An In Situ DRIFTS Study

Investigation of Photocatalytic and Low-Emissivity Properties of TiO 2 :F Films Featuring Columnar Structure Prepared on SnO 2 :F Substrate by Sol–gel Method

Synthesis of High-Activity F-doped TiO2 Photocatalyst Via a Simple One-Step Hydrothermal Process

Preparation and Performance Evaluation of Fluorine Doped Titanium Dioxide Supported on SiO_2

Preparation of visible-light responsive N–F-codoped TiO2 photocatalyst by a sol–gel-solvothermal method

PHOTODEGRADATION OF FORMALDEHYDE OF DOPED TITANIA NANOCRYSTALS PREPARED BY SOL-GEL SYNTHESIS AND HYDROTHERMAL PROCESSING

The Application of Bi‐Doped TiO 2 for the Photocatalytic Oxidation of Formaldehyde

Highly Active Amino-Fullerene Derivative-Modified TiO2 for Enhancing Formaldehyde Degradation Efficiency under Solar-Light Irradiation

Mechanism and Reaction Kinetics of Formaldehyde Oxidation on TiO2: Amorphous Hydroxylated Outperforms Anatase