Abstract:This research took the roasted products obtained by leaching copper (Cu) refining slag using waste acids and roasting leaching residues with calcium oxide (CaO) as raw materials and used oxidative leaching to extract Cu from roasted products using waste acids. Influences of the leaching temperature, liquid–solid ratio, and sulfuric acid (H2SO4) concentration in waste acids on the leaching rate of Cu in the oxidative leaching process of roasted products using waste acids were investigated. The unreacted-core shrinking model of heterogeneous reactions was adopted to reveal the leaching kinetics of Cu in the oxidative leaching process of roasted products using waste acids. Results show that the leaching rate of Cu reaches 91.68% when the leaching temperature, liquid–solid ratio, H2SO4 concentration in waste acids, and injected airflow are 80 ℃, 8:1, 1.5 mol/L, and 200 mL/min, respectively. If the leaching temperature is below 80 ℃, the leaching process of Cu is controlled by the solid-film diffusion, and the apparent activation energy Ea is 11.0835 kJ/mol; at a leaching temperature above 80 ℃, the leaching process of Cu is governed by the interfacial chemical reaction, with an apparent activation energy Ea of 42.3183 kJ/mol. The liquid–solid ratio can positively influence the reaction rate constant. The apparent order of the leaching reaction of Cu is 0.632.

Kinetics of Chromium-Containing Slag Leached by NaCl

Study on Leaching Kinetics of Cr(VI) from Chromium-containing Slag

Adsorption Properties and Kinetics of Chromium from Aqueous Solution by Steel Slag

Selective Leaching of Chromium-Containing Slag by HCl

An Efficient Method of Chromium Extraction from Chromium-Containing Slag with a High Silicon Content

Reduction Kinetics of Chromium(VI) by S(-II) in Alkalescent Aqueous Media

Leaching kinetics of acid-solube Cr(Ⅵ) from chromite ore processing residue in sulfuric acid

Leaching Kinetics and Dissolution Model of Steel Slag in NaOH Solution

Alkali Leaching Kinetics of Amorphous Aluminum Hydroxide Mud in Chromium Hydroxide Residue for Aluminium Recovery

Kinetics of Leaching Vanadium with Acid from Sodium Roasting Calcine of Stone Coal

Leaching Kinetics of Zinc Silicate in Ammonium Chloride Solution

Leaching Kinetics of Magnesium from Spent Magnesia-Chromium Refractories

Chromium enrichment in different crystalline phases of Cr-containing slag under various basicities and equilibrium temperatures

Kinetics of Hexavalent Chromium Removal from Water by Chitosan-Fe0 Nanoparticles.

Kinetics of Leaching Ti-Bearing Slag by Dilute Sulphuric Acid

Static and Dynamic Leaching of Chromium(Vi) from Chromium-Containing Slag

Study on leaching mechanism of hexavalent chromium leaching from chromium residue in salt solutions

Leaching Kinetics of Germanium in Vacuum Slag in Hcl-Cacl2-H2o Solution

Kinetics Study on the Leaching of Copper from Calcification Roasting Copper Refining Slag Using Waste Acid

Oxidative Leaching Kinetics of Vanadium from the Vanadium-Chromium-Reducing Residue with K2Cr2O7

Influencing Factors and Kinetics Analysis of a New Clean Leaching Process for Producing Chromate from Cr–Fe Alloy