Abstract:The low cycle fatigue tests with tension-torsion strain controlling were performed on thin tubular specimens of GH4169 alloy at 650°C. The tension-torsion cyclic stress-strain response and plastic behavior under different load path were studied and the influences of load path and equivalent strain value on fatigue crack propagation were analyzed. The results showed that the shapes of tension-compression and torsion cyclic stress-strain hysteresis loops are related to the loading waves and paths. The phase difference of tension-torsion loading waves causes a turn of the stress-strain hysteresis loop on the component when the component is in elasto-plastic loading stage while the other component has a suddenly load change. The continuous increment of plastic strain during the medial and last cycle stage, which combined with the SEM fractography analysis, was considered by creep. The SEM fractography showed that the load paths and equivalent strain value affected the fracture surface topographies.

Multiaxial fatigue behavior for superalloy GH4169 at high temperature