Abstract:The electro-optic properties and the stability of a cross-linked second order nonlinear optical polymer were reported.This polymer was synthesized via the crosslinking reaction by doping Disperse Red19 moieties into the cellulose diacetate system.The crosslinking temperature is 164 ℃.The spin-coated thin film samples were poled by a corona poling system with a bias-controlled grid at 8 kV.After poling,the electro-optic coefficient was measured to be 4.80 pm/V at 1 550 nm by a Mach-Zehnder interferometer.The stability characteristic was researched by a combination of electro-optic coefficient and dielectric relaxation measurement.The cross-linked electro-optic polymer possesses a good long-time stability.The average relaxation time is 5.3 years and the relaxation was modeled by KWW equation.The dielectric analyses show that the temperature dependence of the relaxation time satisfies the Arrhenius law.

Electro-optic Properties and the Stability of a Cross-linked Second Order Nonlinear Optical Polymer