Influence of cross-linking degree on shape memory effect of styrene copolymer

Zhang Dawei,Lan Xin,Liu Yanjü,Leng Jinsong

DOI: https://doi.org/10.1117/12.715527

2007-01-01

Abstract:This paper is concerned about the synthesis of shape memory styrene copolymer and the investigation of the influence of cross-linking degree on its shape memory effect. As one of novel actuators in smart materials, shape memory polymers (SMPs) have been investigated intensively. Styrene copolymer with proper cross-linking degree can exhibit shape memory effect (SME). In this paper, the influence of cross-linking degree on shape memory effect of styrene copolymer was investigated through altering the dosage of cross-linking agent. The cross-linking degree of styrene copolymer was determined by measuring the gel content. The glass transition temperature (T-g) of styrene copolymer, which is determined the cross-linking degree, was measured by Dynamic Mechanical Analysis (DMA). The shape memory performance of styrene copolymer with different cross-linking degrees was also evaluated. Results indicated that the shape memory polymer (SMP) was synthesized successfully. The Tg increased from 55 degrees C to 80.7 degrees C followed by increasing the gel content from 0% to 80% through increasing the dosage of cross-linking agent from 0% to 4%. Moreover, the SMP experienced good SME and the largest reversible strain of the SMP reached as high as 150%. When heating above T-g+30 degrees C (different copolymers performed different Tg), the shape recovery speed of the copolymers increased with increasing the gel content. However, the recovery speed decreased with increasing the gel content at the same temperature of 95 degrees C.