Abstract:The basal texture of traditional magnesium alloy AZ31 is easy to form and exhibits poor plasticity at room temperature. To address these problems, a multi-micro-alloyed high-plasticity Mg–1.8Zn–0.8Gd–0.1Ca–0.2Mn (wt%) alloy was developed using the unique role of rare earth and Ca solute atoms. In addition, the influence of the annealing process on the grain size, second phase, texture, and mechanical properties of the warm-rolled sheet at room temperature was analyzed with the goal of developing high-plasticity magnesium alloy sheets and obtaining optimal thermal-mechanical treatment parameters. The results show that the annealing temperature has a significant effect on the microstructure and properties due to the low alloying content: there are small amounts of larger-sized block and long string phases along the rolling direction (RD), as well as several spherical and rodlike particle phases inside the grains. With increasing annealing temperature, the grain size decreases and then increases, and the morphology, number, and size of the second phase also change correspondingly. The particle phase within the grains vanishes at 450°C, and the grain size increases sharply. In the full recrystallization stage at 300–350°C, the optimum strength-plasticity comprehensive mechanical properties are presented, with yield strengths of 182.1 and 176.9 MPa, tensile strengths of 271.1 and 275.8 MPa in the RD and transverse direction (TD), and elongation values of 27.4% and 32.3%, respectively. Moreover, there are still some larger-sized phases in the alloy that influence its mechanical properties, which offers room for improvement.

Influence of rolling and annealing treatment on AZ31 magnesium alloys

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Effects of Rolling-Cryogenic Process on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Recrystallization and Anisotropy of AZ31 Magnesium Alloy by Asynchronous Rolling

Effects of cryogenic treatment on microstructure and mechanical properties of AZ31 magnesium alloy rolled at different paths

Microstructure and properties of AZ31 alloy by static recrystallisation at lower temperature

Deformation Microstructure and Characteristics of Cast-Rolling and Normal Rolling AZ31 Magnesium Alloy Sheets

Annealing Behavior Of Rolled Az31 Alloy Sheet

Microstructure, mechanical properties and deformation mechanism of powder metallurgy AZ31 magnesium alloy during rolling

Effect of Final Rolling Speed on Microstructure and Performance of AZ31 Magnesium Alloy Sheet under Small Strain Condition

Influence of cryogenic treatment time on the mechanical properties of AZ31 magnesium alloy sheets after cross-rolling

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Preferential grain growth and textural evolution of AZ31B Mg alloy during annealing after isothermal compression at 400 °C

Grain refining and improving mechanical properties of AZ31 Mg alloy sheets by multi-pass warm rolling with falling temperature

Effect of Final Rolling Temperature on Microstructures and Mechanical Properties of AZ31 Alloy Sheets Prepared by Equal Channel Angular Rolling and Continuous Bending

Effect of Rolling Deformation on Microstructure and Mechanical Properties of As-Cast and Rolled ZM21 Magnesium Alloy

An experimental and theoretical investigation of the effect of second-phase particles on grain growth during the annealing of hot-rolled AZ61 magnesium alloy

Evaluation of static recrystallization and grain growth kinetics of hot-rolled AZ31 alloy

Effect of recrystallization annealing, solid solution and pre-aging intermediate treatment on microstructure and mechanical properties of Al-Mg-Si rolled sheet